Metal coated steel
Why use metal coated steel?
Metal coated steel it’s a cost-efficient method of protecting steel, particularly compared to using stainless steel. It also has environmental benefits since it doesn’t produce emissions and ensures practically maintenance-free use. It’s mostly used unpainted, but if it’s painted the paint coating has good adhesion to the zinc surface.
Because of the sacrificial nature of the zinc, the metal coating provides corrosion protection also for areas of exposed steel surfaces, such as cutting edges and areas where coating has been damaged by scratches or impacts.Full corrosion protection is even achieved in areas that have been heavily formed because there is a low peeling tendency of this low-friction and tightly bonded coating.
Galvanized steel
Where is galvanized steel used?
Galvanized steel is found everywhere, from nuts and bolts to power line pylons and other large-scale installations. Car bodies are nowadays fully galvanized, making them last longer without rusting. The agriculture industry is an extensive user of galvanized sheet metal and galvanized pipe for cattle gates, fences, wires, and much more.
The building industry uses a lot of galvanized steel for infrastructure such as ventilation, heating, and electrical installations. It’s also used for balconies, staircases, ladders, gutters, rails, tubing, and walkways. The aesthetic appearance is another factor which makes it a favorite material for many architects.
450 °C
The temperature at which the base steel is immersed in a bath of molten zinc
80 years
Possible service years of the Z600 coating (42µm on both sides)
>99%
The composition of coating consists almost entirely of zinc
Galvanizing methods
Hot dip galvanization with zinc
Hot dip galvanizing creates a thick, resilient layer of zinc iron alloys on the surface of a steel product. The hot dip process does not generally reduce the strength of the base metal, with the exception of high-strength steels where hydrogen embrittlement can become an issue.
In the process of hot dip galvanizing the base metal is immersed in a bath of molten zinc at a temperature of around 450 °C (842 °F). The zinc alloys with the surface of the steel, forming a matt grey surface that protects the steel from further corrosion.
Hot dip galvanized steel offers a wide protection range from Z100 to Z600 and a tight bond between the hot dip coating and the steel. That’s why zinc coatings are well suited to forming.
The composition of zinc coating consists almost entirely of zinc (>99%) and is lead free, resulting in finely crystallized zinc spangle that meets high requirements for visual appearance. The corrosion resistance provided by the zinc coating is in direct proportion to the coating's thickness. The Z600 coating (42 µm on both sides) can achieve a service life of up to 80 years.
Galvannealed steel coating for excellent corrosion protection
Production of galvannealed steel sheet begins with hot dip galvanization of sheet steel. After passing through the galvanizing zinc bath the sheet steel is heated in an annealing furnace for several seconds. This makes iron and zinc layers diffuse into one another, creating zinc-iron alloy layers at the surface. The galvanizing bath contains slightly over 0.1% aluminum, added to form a layer bonding between the iron and coated zinc. Annealing temperatures are around 500 to 565 °C (932-1049 °F).
Galvannealed coating (ZF) feature excellent spot-welding properties, resulting in longer electrode life and low galling on electrodes. The surface of the galvannealed steel sheet is finely structured, giving an attractive appearance to the painted surface and strong paint adhesion.
Galfan for enhanced formability and corrosion resistance
Galfan (ZA) is a zinc-aluminum alloy coating that provides excellent corrosion protection and forming properties compared to traditional zinc coating.
Galfan steel coating features excellent corrosion resistance compared with traditional zinc coating. This is why it can be used to achieve a longer service life for a steel part, or to replace traditional zinc coating with a thinner galfan coating, thereby simultaneously offering improved weldability and formability properties.
A bright metallic and mildly cellular-patterned surface is characteristic for galfan coating. The eutectic composition of 95% Zn and 5% Al improves the coating adhesion and enables a lamellar coating structure in micro-scale. This makes it ductile and well suited for deep drawing.
Products
Metal coated Docol® AHSS steel
SSAB offers a full selection of hot-dip galvanized, Galfan®, galvannealed, and electrogalvanized coatings for corrosion protection on many of its Docol® AHSS automotive steel grades.
View product
Metal coated SSAB Domex® HSLA and structural steel
SSAB Domex® comes as hot rolledstrip, tubes and section. It's also available in different metal-coated grades for corrosion resistance with zinc, galfan and galvannealed coatings.
View product
Metal coated SSAB Form steels
SSAB Form comes in a wide range of grades, making it easier for you to optimize your production and the performance of the final product. SSAB Form is delivered as hot rolled strip, cold rolled strip, metal-coated grades, and tubes. Delivery condition can be with or without anti-corrosion surface protection.
View product