With its corrosion resistant properties, SSAB Weathering 700 minimizes the need for maintenance and corrosion-prevention treatment, contributing significantly to low maintenance costs throughout the product life cycle.
SSAB Weathering 700 allows for good paint adhesion. The intervals for repainting can be greatly extended compared to plain carbon steel since, if a damage to the paint layer occurs, SSAB Weathering steels have the ability to form a patina layer that minimize corrosion creepage under the paint and inhibits the formation of porous expanding rust.
In addition to low maintenance costs, the reduced need for corrosion prevention means less use of paint and solvents, making SSAB Weathering 700 an environmentally friendly choice of steel.
In manufacturing, the steel contributes to excellent productivity thanks to its good formability, toughness and weldability.
The high-strength of the steel in combination with these properties makes it easier to build lighter and stronger products with increased payload for lower fuel consumption.
Typical applications are containers, railway wagons and many others.
SSAB Weathering 700 is available in thickness 0.80-6.10 mm and width up to 1550 mm as coil, slit coil and cut to length. Length up to 16 meters as cut to length.
||Yield strength Rp0.2
|Tensile strength Rm
|Elongation A80 1)
|Elongation A5 2)
|Min. inner bending radius for a 90° bend
Test direction T = Transverse direction, Test direction L = Longitudinal direction.
Bending properties for both longitudinal and transversal direction.
1) A80 value applies for thicknesses < 3.00 mm.
2) A5 value applies for thicknesses ≥ 3.00 mm.
|Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
The steel is grain refined.
Additional micro alloying elements Nb, V and Ti can be used.
SSAB Weathering is delivered with SSAB Weathering tolerances. Narrower tolerances are available upon request.
Cold rolled: Thickness tolerances in accordance to EN 10131.
Hot rolled Strip: Thickness tolerances correspond to ⅔ of EN 10051 as default value.
Cold rolled: Width and length tolerances in accordance to EN 10131.
Hot rolled Strip: Width and length tolerances according to SSAB standard which offer narrower tolerances compared to EN 10051.
For coil and sheet with mill edge, the width tolerances are corresponding to -0/+20 mm.
For coil and sheet with cut edge, the width tolerances are corresponding to -0/+2 mm.
Length tolerances only apply for cut to length sheets.
Hot rolled Strip: Shape tolerances in accordance to EN 10051. Narrower tolerances according to the SSAB standard are available on request.
Hot rolled Strip:
Flatness tolerances guarantee a maximum flatness deviation of 3 mm/m in addition to the EN 10051 flatness requirements.
Flatness guarantees only apply for cut to length sheets.
Hot rolled strip products: According to EN 10163-2 Class A, Subclass 3.
Cold rolled: Annealed.
Hot rolled Strip: Thermomechanically rolled.
Hot rolled Strip: SSAB Weathering 700 is available with as rolled or pickled surface with mill or cut edge.
SSAB Weathering 700 is not suited for applications requiring hot working or heat treatments at temperatures above 580°C, since the material then may lose its guaranteed properties.
The weldability of SSAB Weathering 700 is good. All the conventional fusion welding methods can be used. To obtain the same corrosion resistance in the weld as in the base metal, special filler metals should be used.
Painting of SSAB weather resistant steel is easy and will result in good paint adhesion. This can further increase the maintenance interval of the component. In order to ensure the uniform colour of the patina, all impurities must be cleaned from the steel surface. Organic impurities such as oil or protective greases must be removed by washing with suitable solvent. Surface oxidation, oxides or rust can be removed by either shot-blasting or pickling. This will also accelerate the patina formation process. Shot-blasting is not recommended for thicknesses below 4 mm. The cleaned surface of the weathering steel can be pre-patinated by allowing the surface to get wet and dry in repeated intervals.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.