Docol® S900MC high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

Get datasheet by email
Close

Get datasheet by email

Tällä sivulla

General Product Description

The high-strength structural steel Docol S900MC is a hot-rolled steel made for cold forming, with a minimum yield strength of 900 MPa. Docol S900MC meets or exceeds the requirements of S900MC in EN 10149-2. Docol S900MC is provided as cut-to-length sheets with excellent thickness accuracy and surface quality. Typical applications include a wide range of components and parts for lighter transport solutions.

Dimension Range

Docol S900MC is available as cut to length sheets with mill edge in thicknesses of 3.00 - 10.00 mm, widths up to 1600 mm and lengths up to 13 meters.

Mechanical Properties

Hide/Show specific columns Edit
Select columns to display
    Thickness
    (mmin)
    Yield strength ReH 1)
    (min MPa)
    Tensile strength Rm
    (MPa)
    Elongation A5
    (min %)
    Min. inner bending radius for a 90° bend 2)
    (x t)
    3.00 - 8.000.118 - 0.315 900 930 - 1200 8 3.0
    8.01 - 10.000.315 - 0.3937 900 930 - 1200 8 3.5
    Compare parameters

    Select one parameter to compare

    Comparison

      The mechanical properties are tested in the longitudinal direction.

      1) If ReH is not applicable then Rp0.2 is used.

      2) For both longitudinal and transverse direction.

      Impact Properties

      Hide/Show specific columns Edit
      Select columns to display
        Product Min. impact energy for longitudinal testing,
        Charpy V 10x10 mm test specimen 1)
        Docol S900MC 27 J / -40 °C
        Compare parameters

        Select one parameter to compare

        Comparison

          Product
          Docol S900MC
          Min. impact energy for longitudinal testing,
          Charpy V 10x10 mm test specimen 1)
          27 J / -40 °C

          1) Impact testing according to EN 10149-2 ( -20 °C /minimum 40J) is available if specified at the time of order.

          Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 5mm. The specified minimum value corresponds to a full-size specimen.

          Chemical Composition (heat analysis)

          Hide/Show specific columns Edit
          Select columns to display
            C
            (max %)
            Si
            (max %)
            Mn
            (max %)
            P
            (max %)
            S
            (max %)
            Nb
            (max %)
            V
            (max %)
            Ti
            (max %)
            0.10 0.25 1.30 0.020 0.010 0.05 1) 0.05 1) 0.07 1)
            Compare parameters

            Select one parameter to compare

            Comparison

              1) Sum of Nb, V and Ti = max 0.22%.

              The steel is grain refined.

              Carbon Equivalent CET(CEV)

              Hide/Show specific columns Edit
              Select columns to display
                Thickness (mmin) 3.00 - 7.990.118 - 0.315 8.00 - 10.000.315 - 0.3937
                Typ CET(CEV) 0.25 (0.50) 0.27 (0.53)
                Compare parameters

                Select one parameter to compare

                Comparison

                  CET and CEV formula

                  Tolerances

                  Hot rolled (UC): Tolerances in accordance to EN 10051.

                  Thickness tolerances 1/2 of EN 10051 category D.

                  Customized dimensional and shape tolerances are available upon request.

                  Surface Treatments

                  Uncoated (UC): available as rolled or pickled and oiled or pickled-dry. As pickled and oiled and pickled-dry up to 5mm thickness.

                  All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

                  Delivery Conditions

                  Docol S900MC is supplied in as rolled surface condition or as pickled surface condition. The product is thermomechanically rolled.

                  Fabrication and Other Recommendations

                  Welding, bending and machining

                  Docol S900MC has good welding, cold forming and cutting performance.

                  Docol S900MC is a cold forming steel not suited for use at temperatures above 400°C since the material may then lose its guaranteed properties.

                   

                  For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

                  Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

                  Docol® High Strength Low Alloy steel product offer

                  Docol® 420LA high strength low alloy

                  Docol HR100XF

                  Docol HR110XF

                  Docol® S600MC high strength low alloy

                  Docol® S650MC high strength low alloy

                  Docol® S700MC high strength low alloy

                  Docol® S900MC high strength low alloy

                  Docol S960MC

                  Docol® 460LA high strength low alloy

                  Docol® 500LA high strength low alloy

                  Docol® 550LA high strength low alloy

                  Docol® 600LA high strength low alloy

                  Docol® 650LA high strength low alloy

                  Docol® 700LA high strength low alloy

                  Muu sisältö