SSAB Multisteel SNL

Datenblatt herunterladen

Allgemeine Produktbeschreibung

Normalized structural steel heavy plate.

SSAB Multisteel SNL is hot rolled structural steel for general steel constructions. SNL = Structural Normalized Low Temperature.

Exceeding the requirements of several standard steel grades, SSAB Multisteel SNL is a versatile structural steel for fabricated products and steel frame structures. Formability and highly consistent quality guarantee fast, uninterrupted production, generating clear savings in the costs of material management.

SSAB Multisteel SNL exceeds several steel standards and is available as six standard steel grades: S355N and S355NL according to EN 10025-3 and S355K2+N, S355J2+N, S355J0+N and S355JR+N according to EN 10025-2.

CE marking:

SSAB Raahe Works is authorized to use the CE marking for structural steels according to EN 10025-2 and EN 10025-3 based on EN 10025-1.

The CE marking is marked on an extra page of inspection certification 3.1.

Abmessungsbereich

SSAB Multisteel SNL is available in thickness of 5.00 - 150.00 mm.

Mechanische Eigenschaften

Dicke
(mmin)
Dicke
(mmin)
5.00 - 16.000.197 - 0.6299
Streckgrenze
(min MPa)
355
Zugfestigkeit
(MPa)
470 - 630
Bruchdehnung A5
(min %)
22
Dicke
(mmin)
Dicke
(mmin)
16.01 - 40.000.6303 - 1.575
Streckgrenze
(min MPa)
345
Zugfestigkeit
(MPa)
470 - 630
Bruchdehnung A5
(min %)
22
Dicke
(mmin)
Dicke
(mmin)
40.01 - 63.001.575 - 2.480
Streckgrenze
(min MPa)
335
Zugfestigkeit
(MPa)
470 - 630
Bruchdehnung A5
(min %)
22
Dicke
(mmin)
Dicke
(mmin)
63.01 - 80.002.481 - 3.150
Streckgrenze
(min MPa)
325
Zugfestigkeit
(MPa)
470 - 630
Bruchdehnung A5
(min %)
21
Dicke
(mmin)
Dicke
(mmin)
80.01 - 100.003.150 - 3.9370
Streckgrenze
(min MPa)
315
Zugfestigkeit
(MPa)
470 - 630
Bruchdehnung A5
(min %)
21
Dicke
(mmin)
Dicke
(mmin)
100.01 - 150.003.9374 - 5.9055
Streckgrenze
(min MPa)
295
Zugfestigkeit
(MPa)
450 - 600
Bruchdehnung A5
(min %)
21

The mechanical properties are tested transverse to the direction of rolling.

Kerbschlagarbeit

SSAB Multisteel SNL

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
27 J / -50 °C

EN 10025-3 S355NL

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
27 J / -50 °C

EN 10025-3 S355N

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
40 J / -20 °C

EN 10025-2 S355K2+N

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
40 J / -20 °C

EN 10025-2 S355J2+N

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
27 J / -20 °C

EN 10025-2 S355J0+N

Mind. Aufprallenergie für Längsprüfung,
Charpy V 10x10- Kerbschlagversuch
27 J / 0 °C

The impact test is made longitudinal to the rolling direction in compliance with EN 10025-1 and EN 10025-2.

Chemische Zusammensetzung (Schmelzenanalyse)

C
(max %)
C
(max %)
0.18
Si
(max %)
0.50
Mn
(max %)
1.60
P
(max %)
0.020
S
(max %)
0.010
Nb
(max %)
0.05

Kohlenstoffäquivalent CEV

Dicke (mmin)
Dicke (mmin)
CEV
(max %)
5.00 - 63.000.197 - 2.480
0.43
63.01 - 150.002.481 - 5.9055
0.45

Toleranzen

Thickness ¾ from EN 10029 Class A.

Width and length according to EN 10029.

Flatness tolerance 4 mm/m.

Surface according to EN 10163-2 Class A subclass 1.

Lieferzustand

Normalized.

Beschichtungen

Shot blasted & primed surface is available upon request.

Certificates

SSAB Multisteel SNL provides three different certificates:

EN 10204-3.1 to SSAB Multisteel SNL.

EN 10204-3.1 +CE to S355NL/N EN 10025-3.

EN 10204-3.1 +CE to S355K2/J2/J0/JR+N EN 10025-2.

Verarbeitung und andere Empfehlungen

Welding:

Weldability is excellent with all welding processes. Increased working temperature requirements are less than those of the corresponding strength grades of standard steels. This means easier welding and cost savings under both workshop and site welding conditions.

Needed working temperatures for thick plates please consult SSAB Tech Support.

Forming:

SSAB Multisteel offers better formability properties than standard steels. Successful forming requires that the manufacturer uses good workshop techniques. Worn tools, poor lubrication, scratches on the surface of the steel as well as edge burrs will all reduce forming quality.

Guaranteed minimum bending radius for all directions is 1.5 x t up to 30 mm thick plate where t = plate thickness.

Heat treatment:

Recommendations for stress relieving and normalizing

Stress relieving 550 – 600°C (target 580°C)

2 minutes/millimeter of thickness, however, 30 minutes minimum. Slow cooling in the furnace.

Normalizing 900 – 940°C (target 920°C)

1 minute/millimeter of thickness, however, 20 minutes minimum. Cooling in free air.

Informationen bezüglich Schweißbarkeit und Verarbeitung finden Sie in den SSAB Broschüren auf www.ssab.com oder kontaktieren Sie die Technische Kundenbetreuung/ Tech Support.

Entsprechende Sicherheits- und Arbeitsschutzvorkehrungen müssen beim Schweißen, Schneiden, Schleifen oder anderen Arbeiten mit dem Produkt getroffen werden.