Docol® S900MC high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

Get datasheet by email
Close

Get datasheet by email

    General Product Description

    The high-strength structural steel Docol S900MC is a hot-rolled steel made for cold forming, with a minimum yield strength of 900 MPa. Docol S900MC meets or exceeds the requirements of S900MC in EN 10149-2. Docol S900MC is provided as cut-to-length sheets with excellent thickness accuracy and surface quality. Typical applications include a wide range of components and parts for heavy trucks.

    Dimension Range

    Docol S900MC is available as cut to length sheets with mill edge in thicknesses of 3.00 - 10.00 mm, widths up to 1600 mm and lengths up to 13 meters.

    Mechanical Properties

    Hide/Show specific columns Edit
    Select columns to display
      Thickness
      (mmin)
      Yield strength ReH 1)
      (min MPa)
      Tensile strength Rm
      (MPa)
      Elongation A5
      (min %)
      Min. inner bending radius for a 90° bend 2)
      (x t)
      3.00 - 8.000.118 - 0.315 900 930 - 1200 8 3.0
      8.01 - 10.000.315 - 0.3937 900 930 - 1200 8 3.5
      Compare parameters

      Select one parameter to compare

      Comparison

        The mechanical properties are tested in the longitudinal direction.

        1) If ReH is not applicable then Rp0.2 is used.

        2) For both longitudinal and transverse direction.

        Impact Properties

        Hide/Show specific columns Edit
        Select columns to display
          Product Min. impact energy for longitudinal testing,
          Charpy V 10x10 mm test specimen 1)
          Docol S900MC 27 J / -40 °C
          Compare parameters

          Select one parameter to compare

          Comparison

            Product
            Docol S900MC
            Min. impact energy for longitudinal testing,
            Charpy V 10x10 mm test specimen 1)
            27 J / -40 °C

            1) Impact testing according to EN 10149-2 ( -20 °C /minimum 40J) is available if specified at the time of order.

            Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 5mm. The specified minimum value corresponds to a full-size specimen.

            Chemical Composition (heat analysis)

            Hide/Show specific columns Edit
            Select columns to display
              C
              (max %)
              Si
              (max %)
              Mn
              (max %)
              P
              (max %)
              S
              (max %)
              Altot
              (min %)
              Nb
              (max %)
              V
              (max %)
              Ti
              (max %)
              0.10 0.25 1.30 0.020 0.010 0.015 0.05 1) 0.05 1) 0.07 1)
              Compare parameters

              Select one parameter to compare

              Comparison

                1) Sum of Nb, V and Ti = max 0.22%.

                The steel is grain refined.

                Carbon Equivalent CET(CEV)

                Hide/Show specific columns Edit
                Select columns to display
                  Thickness (mmin) 3.00 - 7.990.118 - 0.315 8.00 - 10.000.315 - 0.3937
                  Typ CET(CEV) 0.25 (0.50) 0.27 (0.53)
                  Compare parameters

                  Select one parameter to compare

                  Comparison

                    CET and CEV formula

                    Tolerances

                    Hot rolled (UC): Tolerances in accordance to EN 10051.

                    Thickness tolerances 1/2 of EN 10051 category D.

                    Customized dimensional and shape tolerances are available upon request.

                    Surface Treatments

                    Uncoated (UC): available as rolled or pickled and oiled or pickled-dry. As pickled and oiled and pickled-dry up to 5mm thickness.

                    All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

                    Delivery Conditions

                    Docol S900MC is supplied in as rolled surface condition or as pickled surface condition. The product is thermomechanically rolled.

                    Fabrication and Other Recommendations

                    Welding, bending and machining

                    Docol S900MC has good welding, cold forming and cutting performance.

                    Docol S900MC is a cold forming steel not suited for use at temperatures above 400°C since the material may then lose its guaranteed properties.

                     

                    For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

                    Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

                    Docol® High Strength Low Alloy steel product offer

                    Docol® 420LA high strength low alloy

                    Docol® S600MC high strength low alloy

                    Docol® S650MC high strength low alloy

                    Docol® S700MC high strength low alloy

                    Docol® S900MC high strength low alloy

                    Docol® 460LA high strength low alloy

                    Docol® 500LA high strength low alloy

                    Docol® 550LA high strength low alloy

                    Docol® 600LA high strength low alloy

                    Docol® 650LA high strength low alloy

                    Docol® 700LA high strength low alloy

                    Autres sujets dans la même veine