Docol® 600FB ferritic-bainitic
More about Ferritic-Bainitic steelDownload data sheet
Download data sheet
Docol 600FB is a modern hot-rolled advanced high strength steel with a matrix of ferrite or strengthened ferrite containing bainite or strengthened bainite and with a refined grain size.
The steel grade is well suited for cold formed automotive components such as wheels, chassis components and different structural reinforcements. Formability is very good, especially in hole expansion.
Docol HR440Y580T-FB meets the requirements of HR440Y580T-FB according to VDA 239-100.
Hot rolled / UC: thickness 2.00-4.00 mm, width up to 1600 mm.
Hot rolled / GI: thickness 2.00-5.00 mm, width up to 1450 mm.
Slit strip and cut to length sheets are available upon request.
Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
Elongation A5 (min %) |
BH2 (min MPa) |
|
---|---|---|---|---|---|---|---|---|
Docol HR440Y580T-FB | VDA 239-100 | UC, GI* | L | 440 - 600 | 580 - 700 | 15 | 17 | 30 |
*Available upon request.
Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
---|---|---|---|---|---|---|---|---|---|---|---|
Docol HR440Y580T-FB | UC, GI* | 0.18 | 0.50 | 2.00 | 0.050 | 0.010 | 0.015 - 2.00 | 0.15 | 1.00 | 0.010 | 0.20 |
Hot-rolled (UC): Tolerances in accordance to EN 10051.
Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.
Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Coating type | Coating class | Standard | Closest in EN 10346, informative | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) |
---|---|---|---|---|---|
GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 1) | 5.6 - 8.5 |
GI | 50/50 | VDA 239-100 | — | 50 - 70 1) | 7.0 - 9.9 |
GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 |
GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 |
GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 |
GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 |
GA | 40/40 | VDA 239-100 | ZF100 | 40 - 60 1) | 5.6 - 8.5 |
GA | 50/50 | VDA 239-100 | ZF120 | 50 - 80 | 7.0 - 11.3 |
ZA | 95 | EN 10346 | ZA95 | — | 7.0 - |
ZA | 130 | EN 10346 | ZA130 | — | 10.0 - |
EG | 25/25 | EN 10152 | — | 12 - | 1.7 - |
EG | 50/50 | EN 10152 | — | 29 - | 4.1 - |
EG | 75/75 | EN 10152 | — | 47 - | 6.6 - |
EG | 100/100 | EN 10152 | — | 65 - | 9.1 - |
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For hot-dipped (GI, ZA, GA) hot rolled (HR) grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI): available as oiled and/or chemically passivated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Chcesz poznać unikalne zastosowania, wypróbować nowe metody produkcji czy opracować lżejsze komponenty, które poprawią ekonomikę paliwową, wytrzymałość antyzderzeniową i zrównoważony rozwój?
Klienci stosujący Docol® otrzymują całodobowy dostęp do danych dotyczących formowania, pomagających w wyborze materiałów i symulacji procesów produkcji komponentów z zaawansowanej stali motoryzacyjnej o wysokiej wytrzymałości.