Docol® 460LA high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

General Product Description

Docol 460LA is available both as hot rolled and cold rolled. Docol HR460LA-UC can after agreement be adapted and delivered as dual certified with S460MC according to EN 10149-2.

Dimension Range

Cold rolled / UC: thickness 0.50-2.10 mm, width up to 1527 mm.

Cold rolled / GI, GA, ZA: thickness 0.80-2.00 mm, width up to 1410 mm.

Hot rolled / UC: thickness 2.00-6.00 mm, width up to 1600 mm.

Slit strip and cut to length sheets are available upon request.

Grade and coating specific restrictions on available dimensions may occur.

Mechanical Properties

	Standard	Coating	Test direction	Yield strength R_p0.2 (MPa)	Tensile strength R_m (MPa)	Elongation A₈₀¹⁾ (min %)	Elongation A₅³⁾ (min %)	n_10-20/Ag (min)	Min. inner bending radius for a 90° bend⁴⁾
Docol CR460LA	VDA 239-100	UC	L	460 - 580	520 - 680	15	—	0.10	0.5 x t
Docol CR460LA	VDA 239-100	GI, GA, ZA	L	460 - 580	520 - 680	15 ²⁾	—	0.10	1.0 x t
Docol HR460LA	VDA 239-100	UC	L	460 - 560	520 - 640	16	20	—	0.7 x t

Docol CR460LA

Standard

VDA 239-100

Standard

VDA 239-100

Standard

VDA 239-100

* Available upon request.

¹⁾ A₈₀ value applies for thicknesses < 3.00 mm.

²⁾ For GA coatings the minimum elongation value is reduced by 2 units.

³⁾ A₅ value applies for thicknesses ≥ 3.00 mm.

⁴⁾ In some cases tight bending radius may cause micro-cracking of the coating in the bend area. Where design permits, users are encouraged to employ larger radius.

Chemical Composition (ladle analysis)

	Coating	C (max %)	Si (max %)	Mn (max %)	P (max %)	S (max %)	Al (%)	Ti (max %)	Nb (max %)	Cu (max %)
Docol CR460LA	UC	0.10	0.60	1.60	0.025	0.010	From 0.015	0.15	0.09	0.20
Docol CR460LA	GI, GA, ZA	0.13	0.60	1.70	0.030	0.025	From 0.015	0.15	0.10	0.20
Docol HR460LA	UC	0.10	0.50	1.65	0.030	0.025	From 0.015	0.15	0.10	0.20

Docol CR460LA

Coating

GI, GA*, ZA*

Coating

* Available upon request.

Tolerances

Cold rolled (UC): Tolerances in accordance to EN 10131.

Hot rolled (UC): Tolerances in accordance to EN 10051.

Hot-dip galvanized (GI, GA, ZA): Tolerances in accordance to EN 10143.

Customized dimensional and shape tolerances are available upon request.

Coatings

The metal coating options for Docol products include:

Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.

Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.

Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).

Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).

Coating type	Coating class	Standard	Closest in EN 10346, informative	Coating mass per side, single spot test (g/m²)	Thickness per side informative (µm)
GI	40/40	VDA 239-100	Z100	40 - 60	5.6 - 8.5
GI	50/50	VDA 239-100	—	50 - 70	7.0 - 9.9
GI	60/60	VDA 239-100	Z140	60 - 90	8.5 - 12.7
GI	70/70	VDA 239-100	—	70 - 100	9.9 - 14.1
GI	85/85	VDA 239-100	—	85 - 115	12.0 - 16.2
GI	115/115	VDA 239-100	Z275	115 - 155	16.2 - 21.8
GA	40/40	VDA 239-100	ZF100	40 - 60	5.6 - 8.5
GA	50/50	VDA 239-100	ZF120	50 - 80	7.0 - 11.3
ZA	95	EN 10346	ZA95	—	7.0 -
ZA	130	EN 10346	ZA130	—	10.0 -

Coating type

Coating class

40/40

Standard

VDA 239-100

Closest in EN 10346, informative

Z100

Coating mass per side, single spot test (g/m²)

40 - 60

Thickness per side informative (µm)

5.6 - 8.5

Coating type

Coating class

50/50

Standard

VDA 239-100

Closest in EN 10346, informative

—

Coating mass per side, single spot test (g/m²)

50 - 70

Thickness per side informative (µm)

7.0 - 9.9

Coating type

Coating class

60/60

Standard

VDA 239-100

Closest in EN 10346, informative

Z140

Coating mass per side, single spot test (g/m²)

60 - 90

Thickness per side informative (µm)

8.5 - 12.7

Coating type

Coating class

70/70

Standard

VDA 239-100

Closest in EN 10346, informative

—

Coating mass per side, single spot test (g/m²)

70 - 100

Thickness per side informative (µm)

9.9 - 14.1

Coating type

Coating class

85/85

Standard

VDA 239-100

Closest in EN 10346, informative

—

Coating mass per side, single spot test (g/m²)

85 - 115

Thickness per side informative (µm)

12.0 - 16.2

Coating type

Coating class

115/115

Standard

VDA 239-100

Closest in EN 10346, informative

Z275

Coating mass per side, single spot test (g/m²)

115 - 155

Thickness per side informative (µm)

16.2 - 21.8

Coating type

Coating class

40/40

Standard

VDA 239-100

Closest in EN 10346, informative

ZF100

Coating mass per side, single spot test (g/m²)

40 - 60

Thickness per side informative (µm)

5.6 - 8.5

Coating type

Coating class

50/50

Standard

VDA 239-100

Closest in EN 10346, informative

ZF120

Coating mass per side, single spot test (g/m²)

50 - 80

Thickness per side informative (µm)

7.0 - 11.3

Coating type

Coating class

Standard

EN 10346

Closest in EN 10346, informative

ZA95

Coating mass per side, single spot test (g/m²)

—

Thickness per side informative (µm)

7.0 -

Coating type

Coating class

130

Standard

EN 10346

Closest in EN 10346, informative

ZA130

Coating mass per side, single spot test (g/m²)

—

Thickness per side informative (µm)

10.0 -

For hot-dip galvanized (GI, GA, ZA) hot rolled grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.

Docol metal coated products are available with surface quality for unexposed applications.

In addition to these coating masses, OEM specific coatings are available upon request.

Surface Treatments

Uncoated (UC): available as oiled.

Hot-dip galvanized (GI, GA, ZA): available as oiled and/or chemically passivated.

All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr⁶⁺). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

Fabrication and Other Recommendations

For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

Docol® High Strength Low Alloy steel product offer

Autres sujets dans la même veine

Stock de matières d'essai

Vous voulez découvrir des applications automobiles uniques, essayer de nouvelles méthodes de production, ou créer des pièces plus légères pour améliorer l'efficacité énergétique, la résistance aux chocs et la durabilité ?

Informations sur le formage des aciers Docol® AHSS

Les clients Docol® peuvent profiter d'un accès 24h sur 24, 7 jours sur 7, à toutes les informations sur le formage, qui peuvent servir à des simulations intégrant des aciers automobiles avancés à haute limite élastique.

General Product Description

Dimension Range

Mechanical Properties

Chemical Composition (ladle analysis)

Tolerances

Coatings

Surface Treatments

Fabrication and Other Recommendations

Docol® High Strength Low Alloy steel product offer

Docol® 420LA high strength low alloy

Docol HR100XF

Docol HR110XF

Docol® S600MC high strength low alloy

Docol® S650MC high strength low alloy

Docol® S700MC high strength low alloy

Docol® S900MC high strength low alloy

Docol S960MC