Strenx® 900MC
Download data sheet
Download data sheet
The high-strength structural steel at 900 MPa
Strenx® 900MC is a hot-rolled structural steel made for cold forming, with a minimum yield strength of 900 MPa.
Strenx® 900MC meets and exceeds the requirements of S900MC in EN 10149-2. These cut-to-length sheets feature excellent thickness accuracy and surface quality in relation to strength level, providing an outstanding finish to the final products. Typical applications include advanced lifting devices and lighter transport solutions and components.
The mechanical properties are tested in the longitudinal direction.
1) If ReH is not applicable then Rp0.2 is used.
2) For both longitudinal and transverse direction.
1) Impact testing according to EN 10149-2 ( -20 °C /minimum 40J) is available if specified at the time of order.
Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 5mm. The specified minimum value corresponds to a full-size specimen.
1) Sum of Nb, V and Ti = max 0.22%.
The steel is grain refined.
Tolerances according to Strenx® Thickness Guarantee.
Strenx® Guarantees offer considerably narrower thickness tolerances compared to EN 10051.
Width and length tolerances according to SSAB standard.
SSAB standard offer narrower width and length tolerances compared to EN 10051.
Length tolerances only apply for cut to length sheets.
Tolerances according to EN 10051. Narrower tolerances according to the SSAB standard are available on request.
Tolerances according to Strenx® Flatness Guarantee Class A.
Strenx® Flatness Guarantee offer narrower tolerances compared to EN 10051.
Flatness guarantees only apply for cut to length sheets.
According to EN 10163-2 Class A, Subclass 3.
Strenx® 900MC is supplied in as rolled surface condition, pickled surface is available in a limited thickness range. The product is thermomechanically rolled.
Delivery requirements can be found in SSAB’s brochure Strenx® Guarantees or on www.ssab.com.
Strenx® 900MC has good welding, cold forming and cutting performance.
Strenx® 900MC is a cold forming steel not suited for heat treatments at temperatures above 400°C since the material then may lose its guaranteed properties.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.