Proven performance

Duroxite^® 100

Sliding Wear

Wear part: Drum mixer paddles of Duroxite^® 101
Industry: Concrete – Canada
Application: Drum mixer
Replacing 1" polyurethane paddles with Duroxite^® 101 6 mm on 10 mm(¼" on 3/8")
Service life: 5 times longer service life

Duroxite^® 200

Severe Sliding Wear

Wear part: Liner plate made of Duroxite^®200
Industry: Coal terminal – Canada
Application: Coal chute
Replacing a competitor’s CCO 6 mm on 6 mm (¼’’ on ¼’’) with Duroxite^® 200 6mm + 6mm (¼’’ on ¼’’)
Service life: Increased service life from 6 to 30 month

Duroxite^® 300

Extreme Sliding Wear

Wear part: Conveyor liner plate using Duroxite^® 300
Industry: Steel foundry – Mexico
Application: Conveyor
The original conveyor liner made of casting Mn with tungsten carbide 38mm (1.5”) worn out after three months. It’s replaced by Duroxite^® 300 12 mm + 6 mm (1/4’’ on 1/2’’) welded on 20mm (¾’’) Hardox^® 600.
After three months, this liner plate onlyshowed 0.254 mm (0.01”) wear.
Service life: The service life of Duroxite^® 300 plate is about 2 years.

Duroxite^® 400

Heat and Metal-To-Metal wear

Wear part: Bail pin made of Duroxite^® 400 Pin
Industry: Coal mine – USA
Application: Dragline bucket
The previously used induction hardened 4340 pin was replaced by a Duroxite^® 400 overlay pin.
Service life: Increased service life from 800 to 3,500 hours

Duroxite^® 500

High impact & Sliding Wear

Wear part: Liner plate made of Duroxite^® 500
Industry: Copper mine – China
Application: Belt machine
Duroxite^® 500 6 mm on 41 mm (¼" on 1-5/8") replaced the ZG M13 cast liner plate (50 mm)
Service life: Increased from 15 to 45 days