Docol® 600LA high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

General Product Description

The Docol 600LA is a high-strength low-alloy steel that offer consistent properties for modern, rapid production methods. Typical applications include components and parts such as load-bearing structures, for example chassis. Docol HR600LA-UC can after agreement be adapted and delivered as dual certified with S600MC according to EN 10149-2.

Dimension Range

Hot rolled / UC: thickness 2.00-6.00 mm, width up to 1600 mm.

Slit strip and cut to length sheets are available upon request.

Grade and coating specific restrictions on available dimensions may occur.

Mechanical Properties

	Standard	Coating	Test direction	Yield strength R_p0.2 (MPa)	Tensile strength R_m (MPa)	Elongation A₈₀ (min %)	Elongation A₅ (min %)	Min. inner bending radius for a 90° bend
Docol HR600LA	SSAB	UC	L	600 - 730	650 - 820	13 ¹⁾	16 ²⁾	1.1 x t

Docol HR600LA

Standard

SSAB

Coating

Test direction

Yield strength R_p0.2
(MPa)

600 - 730

Tensile strength R_m
(MPa)

650 - 820

Elongation A₈₀
(min %)

13 ¹⁾

Elongation A₅
(min %)

16 ²⁾

Min. inner bending radius for a 90° bend

1.1 x t

¹⁾ A₈₀ value applies for thicknesses < 3.00 mm.

²⁾ A₅ value applies for thicknesses ≥ 3.00 mm.

Chemical Composition (ladle analysis)

	Coating	C (max %)	Si (max %)	Mn (max %)	P (max %)	S (max %)	Al (%)	Ti (max %)	Nb (max %)	Cu (max %)
Docol HR600LA	UC	0.12	0.60	1.90	0.025	0.010	From 0.015	0.15	0.09	0.20

Docol HR600LA

Coating

C
(max %)

0.12

Si
(max %)

0.60

Mn
(max %)

1.90

P
(max %)

0.025

S
(max %)

0.010

Al
(%)

From 0.015

Ti
(max %)

0.15

Nb
(max %)

0.09

Cu
(max %)

0.20

Tolerances

Hot rolled (UC): Tolerances in accordance to EN 10051.

Customized dimensional and shape tolerances are available upon request.

Surface Treatments

Uncoated (UC): available as oiled.

All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr⁶⁺). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

Fabrication and Other Recommendations

For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

Docol® High Strength Low Alloy steel product offer

Conteúdo relacionado

Estoque de amostras

Quer descobrir aplicações automotivas exclusivas, experimentar novos métodos de produção ou criar componentes mais leves e capazes de aumentar a eficiência do combustível, de resistir a colisões e com melhor sustentabilidade?

Dados de conformação para os aços AHSS Docol®

Os clientes existentes do Docol® têm acesso 24 horas por dia, 7 dias por semana aos dados de conformação necessários para ajudá-los na seleção e simulação de aços automotivos avançados de alta resistência.

General Product Description

Dimension Range

Mechanical Properties

Chemical Composition (ladle analysis)

Tolerances

Surface Treatments

Fabrication and Other Recommendations

Docol® High Strength Low Alloy steel product offer

Docol® 420LA high strength low alloy

Docol HR100XF

Docol HR110XF

Docol® S600MC high strength low alloy

Docol® S650MC high strength low alloy

Docol® S700MC high strength low alloy

Docol® S900MC high strength low alloy

Docol S960MC

Docol® 460LA high strength low alloy

Docol® 500LA high strength low alloy

Docol® 550LA high strength low alloy