Duroxite® Roller Wire is a flux-cored welding wire for roller repair in the cement and power industries using an open-arc welding process. The weld deposit contains abrasion-resistant material which is composed of a high proportion of extremely hard primary M7C3 chromium-rich carbides with a typical hardness of 1700 HK*). The carbides are dispersed evenly in a ductile eutectic austenite matrix. Besides a rich chromium content in the wire, additional molybdenum is added to improve overlay toughness, strengthen the matrix, and refine the carbides’ size to increase abrasion resistance and extend service life. The Duroxite® Roller Wire is designed for refurbishing worn rollers with stringer bead welding. The wire is suitable for welding on curved surfaces, and it is feasible to deposit multiple layers up to 75mm (3’’) thick. Preheating, interpass temperature, and post-weld heat treatment are as needed according to the base metal recommendations. It naturally reveals stress-relief cracks after welding.

*) HK is the Knoop microhardness used primarily for very brittle materials.

Key Benefits

  • Same wear resistance guaranteed from surface through 75% depth of the overlay.
  • Optimal alloy formulation that forms a carbide composition which provides a good combination of wear resistance and homogenous bonding.
  • Feasible to weld up to 75mm (3’’) thick to rebuild worn rollers with extreme wear back to their original design.

Typical Applications

Duroxite® Roller Wire is mainly designed to repair roller wear parts which work at temperatures up to 350ºC (660ºF). Typical examples include cement vertical mill rollers and coal pulverizer rollers.

Standard Dimensions

Hide/Show specific columns Edit
Select columns to display
    Standard diameter
    Imperial
    7/64"
    Compare parameters

    Select one parameter to compare

    Comparison

      Standard diameter
      Imperial
      7/64"

      Mechanical Properties

      Hide/Show specific columns Edit
      Select columns to display
        ASTM G65 – Procedure A weight loss 2)
        Typical weld metal surface
        hardness 1)
        Number of overlay passes Surface
        (g max)
        75 % depth of overlay 3)
        (g max)
        Hardness: 3-layer deposit on mild steel
        Multiple passes 0.18 0.18 58 - 63 HRC
        Compare parameters

        Select one parameter to compare

        Comparison

          1) Surface hardness is measured on machined flat surface just below overlay surface.

          2) ASTM G65 is a standard test measuring sliding abrasion resistance using a dry sand/rubber wheel apparatus. ASTM G65-Procedure A is the most severe test method.

          3) ASTM G65 wear test is conducted at 75% depth of the overlay materials to ensure consistently good wear resistance from the top surface through to the depth of 75% of the overlay.

          Test results for mechanical properties

          Test results for mechanical properties, deposit overlay chemical composition, surface hardness, and ASTM G65-A weight loss were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, substrate chemistry and working temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended applications.

          Chemical Composition

          Hide/Show specific columns Edit
          Select columns to display
            Typical all-weld metal analysis (Weight %)
            C
            (%)
            Mn
            (%)
            Si
            (%)
            Cr
            (%)
            Mo
            (%)
            Fe
            4.5 0.5 0.5 27.0 0.8 Balance
            Compare parameters

            Select one parameter to compare

            Comparison

              Microstructure

              The microstructure of Duroxite® Roller Wire is composed of a high proportion of extremely hard primary M7C3 chromium-rich carbides with a typical hardness of 1700 HK dispersed evenly in a ductile eutectic austenite matrix. The volume fraction of primary carbides is maintained between 30 to 50% to provide a good combination of wear resistance and homogenous bonding.

              Welding recommendations

              Hide/Show specific columns Edit
              Select columns to display
                Welding conditions
                Current type Shielding gas Welding positions
                DCEP (Direct current electrode positive) None (Self-shielded) Flat, half up, half down
                Compare parameters

                Select one parameter to compare

                Comparison

                  Welding parameters recommendations

                  Hide/Show specific columns Edit
                  Select columns to display
                    Diameter
                    Amperage (A)
                    Voltage (V)
                    Stick-out
                    Imperial Range Optimum Range Optimum Range Optimum
                    7/64" 300 - 450 400 28 - 32 30 5/8" - 1 3/16" 1"
                    Compare parameters

                    Select one parameter to compare

                    Comparison

                      Recovery: 90%

                      Delivery Conditions

                      Hide/Show specific columns Edit
                      Select columns to display
                        Standard package
                        Diameter
                        Weight
                        Type Imperial Imperial
                        Drum 7/64" 440 lbs
                        Compare parameters

                        Select one parameter to compare

                        Comparison

                          Fabrication and Other Recommendations

                          The welded overlay components can be processed by welding, cutting, forming and machining. Specific recommendations can be found in the Duroxite® Product brochure or by consulting your local technical support representative.

                          Safety precautions

                          When welding or cutting Duroxite® products, gases and harmful fumes are produced that are chemically complex and difficult to classify. The major toxic component in the fumes is hexavalent chromium. The proper exhaust ventilation equipment and fume-extraction torches are recommended, as well as suitable protective clothing and respiratory protection for operators.