Strenx® 100 is a structural steel with a minimum yield strength of 100 ksi. Strenx® 100 meets the requirements of ASTM A514, Grade S,
for thicknesses up to 2 1/2 inch.
Strenx® 100 is supplied in plate thicknesses of 3/16 - 5 inches. More detailed information on dimensions is provided in the dimension program at www.ssab.com.
1) For transverse test pieces according to ASTM A6 and A370.
2) For 1-1/2” wide tension test samples. If 1/2” round samples are used, the minimum RA is 45%.
1) Average of three tests. Single value min 2/3 of specified average.
For thicknesses between 0.236" - 0.469", sub-size Charpy V-specimens are used. The specified minimum value is then proportrional to the cross-sectional area of the specimen compared to a full-size specimen (0.393x0.393").
Impact testing according to ASTM A6, per heat and 45 metric tons.
The steel is grain refined. *) Intentional alloying elements.
More details are given in SSAB’s brochure Strenx® Guarantees.
Tolerances according to Strenx® Thickness Guarantees.
Strenx® Guarantees meets the requirements of EN 10029 Class A, but offers narrower tolerances.
EN 10029 meets and exceeds the requirements for ASTM A6.
Tolerances on length and width according to ASTM A6.
Tolerances according to ASTM A6.
Tolerances on flatness according to Strenx® Flatness guarantee Class C, which are twice as good as the ASTM A6 flatness requirements.
According to ASTM A6.
The delivery condition is Quenched and Tempered. The plates are delivered with sheared or thermally cut edges. Untrimmed edges after agreement.
Delivery requirements can be found in SSAB’s brochure Strenx® Guarantees.
Recommendations are found in SSAB’s brochures at www.ssab.com or consult Tech Support.
Workshop guidelines for Strenx® 100 refer to the same recommendations as for Strenx® 700. Bending guarantees according to Strenx® bending guarante class A.
Strenx® 100 has obtained its mechanical properties by quenching and subsequent tempering. The properties of the delivery condition cannot be retained after exposure to temperatures in excess of 580ºC.
Appropriate health and safety precautions must be taken when welding, cutting, grinding or otherwise working on this product. Grinding, especially of primer coated plates, may produce dust with a high particle concentration.