Docol® S600MC high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

Get datasheet by email
Close

Get datasheet by email

On this page

General Product Description

The high-strength structural steel Docol S600MC is a hot-rolled steel made for cold forming, with a minimum yield strength of 600 MPa for stronger and lighter structures. Docol S600MC meets or exceeds the requirements of S600MC in EN 10149-2. Typical applications include a wide range of heavy trucks components and parts, such as frame rails and cross-members. Docol S600MC comes in coils, slit coils and cut-to-length sheets.

Dimension Range

Hot rolled / UC: thickness 2.00-10.00 mm, width up to 1600 mm.

Slit strip and cut to length sheets are available upon request.

Mechanical Properties

Hide/Show specific columns Edit
Select columns to display
    Thickness
    (mm)
    Standard Coating Test direction
    Yield strength ReH 1)
    (min MPa)
    Tensile strength Rm
    (MPa)
    Elongation A80 2)
    (min %)
    Elongation A5 3)
    (min %)
    Min. inner bending radius for a 90° bend 4)
    (x t)
    2.00 - 3.00 SSAB UC L 600 650 - 820 13 16 0.7
    3.01 - 6.00 SSAB UC L 600 650 - 820 16 1.1
    6.01 - 10.00 SSAB UC L 600 650 - 820 16 1.4
    Compare parameters

    Select one parameter to compare

    Comparison

      1) If ReH is not applicable then Rp0.2 is used.

      2) A80 value applies for thicknesses < 3.00 mm.

      3) A5 value applies for thicknesses ≥ 3.00 mm.

      4) For both longitudinal and transverse direction.

      Impact Properties

      Hide/Show specific columns Edit
      Select columns to display
        Product Min. impact energy for longitudinal testing,
        Charpy V 10x10 mm test specimen
        Docol S600MC D 40 J / -20 °C
        Docol S600MC E 27 J / -40 °C
        Compare parameters

        Select one parameter to compare

        Comparison

          Product
          Docol S600MC D
          Min. impact energy for longitudinal testing,
          Charpy V 10x10 mm test specimen
          40 J / -20 °C
          Product
          Docol S600MC E
          Min. impact energy for longitudinal testing,
          Charpy V 10x10 mm test specimen
          27 J / -40 °C
          Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 6mm. The specified minimum value corresponds to a full-size specimen.

          Chemical Composition (heat analysis)

          Hide/Show specific columns Edit
          Select columns to display
            C
            (max %)
            Si
            (max %)
            Mn
            (max %)
            P
            (max %)
            S
            (max %)
            Nb
            (max %)
            V
            (max %)
            Ti
            (max %)
            0.12 0.21 1) 1.90 0.025 0.010 0.09 2) 0.20 2) 0.15 2)
            Compare parameters

            Select one parameter to compare

            Comparison

              1) If the material is to be hot-dip galvanized, this must be specified in the order. Galvanizing class A available upon request.

              2) Sum of Nb, V and Ti = max 0.22%.

              The steel is grain refined.

              Carbon Equivalent CET(CEV)

              Hide/Show specific columns Edit
              Select columns to display
                Thickness (mm) 2.00 - 10.00
                Typ CET(CEV) 0.21 (0.33)
                Compare parameters

                Select one parameter to compare

                Comparison

                  Thickness (mm)
                  Typ CET(CEV)
                  2.00 - 10.00
                  0.21 (0.33)
                  CET and CEV formula

                  Tolerances

                  Hot rolled (UC): Tolerances in accordance to EN 10051.

                  Customized dimensional and shape tolerances are available upon request.

                  Surface Treatments

                  Uncoated (UC): available as black or pickled and oiled.

                  All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

                  Fabrication and Other Recommendations

                  For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

                  Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

                  Docol® High Strength Low Alloy steel product offer

                  Docol® 420LA high strength low alloy

                  Docol HR100XF

                  Docol HR110XF

                  Docol® S600MC high strength low alloy

                  Docol® S650MC high strength low alloy

                  Docol® S700MC high strength low alloy

                  Docol® S900MC high strength low alloy

                  Docol S960MC

                  Docol® 460LA high strength low alloy

                  Docol® 500LA high strength low alloy

                  Docol® 550LA high strength low alloy

                  Docol® 600LA high strength low alloy

                  Docol® 650LA high strength low alloy

                  Docol® 700LA high strength low alloy

                  Related content