General Product Description
Docol 600DH trip assisted dual-phase steel provides improved formability and comparable weldability to traditional dual-phase steels. Its suitability for car safety and structural components are supported not only by deep drawability but also by enhanced edge formability.
This steel undergoes a special heat treatment producing mainly two-phase structure. Ferrite that imparts unique forming properties represents one phase and martensite that accounts for the strength represents the other phase. Small amounts of bainite and retained austenite improve formability further.
Dimension Range
Cold rolled / GI: thickness 0.80-2.40 mm, width up to 1400 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Mechanical Properties
Hide/Show specific columns Edit
Select columns to display
| Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
n4-6 (min) |
n10-20/Ag (min) |
BH2 (min MPa) |
|
|---|---|---|---|---|---|---|---|---|---|
| Docol CR330Y590T-DH | SSAB | GI | L | 330 - 430 | 590 - 700 | 26 | 0.20 | 0.16 | 30 |
Compare parameters
Select one parameter to compare
Comparison
Docol CR330Y590T-DH
Standard
SSAB
Coating
GI
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
330 - 430
Tensile strength Rm
(MPa)
(MPa)
590 - 700
Elongation A80
(min %)
(min %)
26
n4-6
(min)
(min)
0.20
n10-20/Ag
(min)
(min)
0.16
BH2
(min MPa)
(min MPa)
30
Expand
Collapse
Chemical Composition (ladle analysis)
Hide/Show specific columns Edit
Select columns to display
| Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
|---|---|---|---|---|---|---|---|---|---|---|---|
| Docol CR330Y590T-DH | GI | 0.15 | 0.80 | 2.50 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 |
Compare parameters
Select one parameter to compare
Comparison
Docol CR330Y590T-DH
Coating
GI
C
(max %)
(max %)
0.15
Si
(max %)
(max %)
0.80
Mn
(max %)
(max %)
2.50
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Tolerances
Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
Coatings
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Hide/Show specific columns Edit
Select columns to display
| Coating type | Coating class | Standard | Closest in EN 10346, informative | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) | Density (g/cm3) | Surface quality (U = unexposed, E = exposed) |
|---|---|---|---|---|---|---|---|
| GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 1) | 5.6 - 8.5 | 7.1 | U |
| GI | 50/50 | VDA 239-100 | — | 50 - 70 1) | 7.0 - 9.9 | 7.1 | U |
| GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 | 7.1 | U |
| GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 | 7.1 | U |
| GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 | 7.1 | U |
| GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 | 7.1 | U |
Compare parameters
Select one parameter to compare
Comparison
Coating type
GI
Coating class
40/40
Standard
VDA 239-100
Closest in EN 10346, informative
Z100
Coating mass per side, single spot test (g/m2)
40 - 60 1)
Thickness per side informative (µm)
5.6 - 8.5
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
Coating type
GI
Coating class
50/50
Standard
VDA 239-100
Closest in EN 10346, informative
—
Coating mass per side, single spot test (g/m2)
50 - 70 1)
Thickness per side informative (µm)
7.0 - 9.9
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
Coating type
GI
Coating class
60/60
Standard
VDA 239-100
Closest in EN 10346, informative
Z140
Coating mass per side, single spot test (g/m2)
60 - 90
Thickness per side informative (µm)
8.5 - 12.7
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
Coating type
GI
Coating class
70/70
Standard
VDA 239-100
Closest in EN 10346, informative
—
Coating mass per side, single spot test (g/m2)
70 - 100
Thickness per side informative (µm)
9.9 - 14.1
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
Coating type
GI
Coating class
85/85
Standard
VDA 239-100
Closest in EN 10346, informative
—
Coating mass per side, single spot test (g/m2)
85 - 115
Thickness per side informative (µm)
12.0 - 16.2
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
Coating type
GI
Coating class
115/115
Standard
VDA 239-100
Closest in EN 10346, informative
Z275
Coating mass per side, single spot test (g/m2)
115 - 155
Thickness per side informative (µm)
16.2 - 21.8
Density (g/cm3)
7.1
Surface quality (U = unexposed, E = exposed)
U
Expand
Collapse
In addition to these coating masses, asymmetric coatings and OEM coating specifications are available upon request.
1) For hot-dipped (GI, ZA, GA) hot rolled (HR) grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.
Surface Treatments
Hot-dip galvanized (GI): available as oiled and/or chemically passivated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
Fabrication and Other Recommendations
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Docol® dual phase with high formability steel product offer
Docol® 600DH dual phase with high formability
Docol® 800DH dual phase with high formability
Conteúdo relacionado
-
Estoque de amostras
Quer descobrir aplicações automotivas exclusivas, experimentar novos métodos de produção ou criar componentes mais leves e capazes de aumentar a eficiência do combustível, de resistir a colisões e com melhor sustentabilidade?
-
Dados de conformação para os aços AHSS Docol®
Os clientes existentes do Docol® têm acesso 24 horas por dia, 7 dias por semana aos dados de conformação necessários para ajudá-los na seleção e simulação de aços automotivos avançados de alta resistência.