Toolox® 44

Descargar ficha de datos

Seleccionar idioma

Get datasheet by email
Close

Get datasheet by email

    Descripción general del producto

    Toolox® 44 is a steel already heat treated to the final properties.Thus saving time, costs and risks associated with heat treatment.

    The very high strength is combined with a high and guaranteed toughness as well as an excellent fatigue resistence. Making Toolox® 44 the ideal choice for the most demanding engineering and mould and die applications.

    Toolox® 44 can be surface hardened with methods like nitriding, laser and induction. Giving the possibilities to even further improve the performance.

    Rango de dimensiones

    Toolox® 44 is available as plates in thicknesses between 6.0 - 130.0 mm. Other dimensions can be available on request.

    Propiedades mecánicas

    Ocultar/mostrar columnas específicas Editar
    Seleccionar columnas para mostrar
      Espesor
      (mm)
      Dureza 1)
      (HBW)
      Límite de elasticidad Rp0,2
      (min MPa)
      Tensión de rotura Rm
      (mín. MPa)
      Elongación A5
      (min %)
      6.0 - 130.0 410 - 475 1150 1300 8
      Comparar parámetros

      Seleccione un parámetro para comparar

      Comparativa

        1) Se mide la dureza, conforme a EN ISO 6506-1, en una superficie fresada de entre 0,5 y 2 mm por debajo de la superficie de la chapa.

        Propiedades de impacto

        Ocultar/mostrar columnas específicas Editar
        Seleccionar columnas para mostrar
          Espesor
          (mm)
          Ensayo transversal, mín. energía de impacto,
          Charpy V probetas 10x10 mm 1)
          6.0 - 130.0 18 J / 20 °C
          Comparar parámetros

          Seleccione un parámetro para comparar

          Comparativa

            Espesor
            (mm)
            6.0 - 130.0
            Ensayo transversal, mín. energía de impacto,
            Charpy V probetas 10x10 mm 1)
            18 J / 20 °C

            1) A no ser que se indique lo contrario, se realizarán ensayos de impacto transversal de conformidad con EN 10025-6, opción 30. Para espesores de entre 6.0 - 11.9 mm, se usan probetas de Charpy V de tamaños inferiores. Elvalor mínimo especificado es en ese caso proporcional al área transversal de la probeta (muestra) en comparación con una probeta de tamaño estándar (10 x 10 mm).

             

             

             

            Ultrasonic testing

            Ultrasonic inspection is carried out according to : EN 10 160 with extra demands according to specification SSAB V6.

            Tolerancias

            More details are given in SSAB’s brochure Toolox® Guarantees and on www.toolox.com.

            Espesor

            Tolerances according to Toolox® Thickness Guarantee.

            Toolox® Guarantees meets the requirements of EN 10029 Class C but offers more narrow tolerances.

            Largo y ancho

            Tolerances according to EN 10029.

            Planitud

            Tolerances are according to Toolox® Flatness Guarantees, which are more restrictive than EN 10029 Class N (steel type L).

            Propiedades superficiales

            De conformidad con la norma EN 10163-2, clase B, subclase 3.

            Condiciones de entrega

            Quenched and Tempered at a minimum temperature of 590 °C.

            On delivery from SSAB the plates meet the following specifications:

            • Free from mill scale
            • Not repair welded

            Delivery requirements can be found in SSAB’s brochure Toolox® Guarantees or at www.toolox.com.