Docol 1200CP complex phase steel is developed for increased safety in cars. Its ultra-high strength combined with an improved formability allows for weight reduction in BIW applications. This steel undergoes special heat treatment in a continuous annealing or galvanizing line, producing a complex phase structure.
Cold rolled / UC, EG: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI: thickness 1.00-1.70 mm, width up to 1350 mm.
Slit strip are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
||Yield strength Rp0.2
|Tensile strength Rm
|Docol CR900Y1180T-CP||VDA 239-100||UC, EG, GI*||L||900 - 1100||1180 - 1350||5||30|
The testing of mechanical properties of electrogalvanized products is conducted without coating.
* Available upon request
|Docol CR900Y1180T-CP||UC, EG, GI*||0.23||1.00||2.90||0.050||0.010||0.015 - 1.00||0.15||1.00||0.005||0.20|
Cold rolled (UC, EG): Tolerances in accordance to EN 10131.
Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
|Coating type||Coating class||Standard||Closest in EN standard, informative 1)||Coating mass per side, single spot test (g/m2)||Thickness per side informative (µm)|
|GI||40/40||VDA 239-100||Z100||40 - 60||5.6 - 8.5|
|GI||50/50||VDA 239-100||—||50 - 70||7.0 - 9.9|
|GI||60/60||VDA 239-100||Z140||60 - 90||8.5 - 12.7|
|GI||70/70||VDA 239-100||—||70 - 100||9.9 - 14.1|
|GI||85/85||VDA 239-100||—||85 - 115||12.0 - 16.2|
|GI||115/115||VDA 239-100||Z275||115 - 155||16.2 - 21.8|
|EG||12/12||VDA 239-100||ZE25/25||12 - 32||1.7 - 4.5|
|EG||18/18||VDA 239-100||—||18 - 38||2.5 - 5.4|
|EG||29/29||VDA 239-100||ZE50/50||29 - 49||4.1 - 6.9|
|EG||47/47||VDA 239-100||ZE75/75||47 - 61||6.6 - 8.6|
|EG||50/50||VDA 239-100||—||50 - 70||7.0 - 9.9|
|EG||53/53||VDA 239-100||—||53 - 73||7.5 - 10.3|
|EG||60/60||VDA 239-100||—||60 - 80||8.5 - 11.3|
|EG||65/65||VDA 239-100||ZE100/100||65 - 85||9.2 - 12.0|
|EG||70/70||VDA 239-100||—||70 - 90||9.9 - 12.7|
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For GI and GA the closest informative value refers to EN 10346. For EG to EN 10152.
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI): available as oiled and/or chemically passivated.
Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.