Toolox 33

Toolox® 33

Descargar ficha de datos

Seleccionar idioma

    Descripción general del producto

    The pre-hardened, exceptionally clean tool and engineering steel.

    Thanks to its low carbon and alloy content, Toolox® 33 is perfectly adaptable for welding as well as hot cutting. Giving the possibility to product components more cost efficient by saving machining time.

    Delivered in quenched and tempered condition, Toolox 33 features high impact toughness and very low residual stresses to achieve good dimensional stability after machining. Toolox® 33 is suitable for mold and dies as well as tooling and engineering components. By using the proper surface engineering methods, you can significantly extend the service life of your tools and components.

    Rango de dimensiones

    Toolox® 33 is available as plates in thicknesses between 6.0 - 130.0 mm. Other dimensions can be available on request.

    Propiedades mecánicas

    Ocultar/mostrar columnas específicas Editar
    Seleccionar columnas para mostrar
      Espesor
      (mm)      		 Dureza 1)
      (HBW)      		 Límite de elasticidad Rp0,2
      (min MPa)      		 Tensión de rotura Rm
      (mín. MPa)      		 Elongación A5
      (min %)
      6.0 - 130.0 275 - 325 700 800 10
      Comparar parámetros

      Seleccione un parámetro para comparar

      Comparativa

        1) Se mide la dureza, conforme a EN ISO 6506-1, en una superficie fresada de entre 0,5 y 2 mm por debajo de la superficie de la chapa.

        Propiedades de impacto

        Ocultar/mostrar columnas específicas Editar
        Seleccionar columnas para mostrar
          Espesor
          (mm)          		 Ensayo transversal, mín. energía de impacto,
          Charpy V probetas 10x10 mm 1)
          6.0 - 130.0 35 J / 20 °C
          Comparar parámetros

          Seleccione un parámetro para comparar

          Comparativa

            Espesor
            (mm)
            6.0 - 130.0
            Ensayo transversal, mín. energía de impacto,
            Charpy V probetas 10x10 mm 1)
            35 J / 20 °C

            1) A no ser que se indique lo contrario, se realizarán ensayos de impacto transversal de conformidad con EN 10025-6, opción 30. Para espesores de entre 6.0 - 11.9 mm, se usan probetas de Charpy V de tamaños inferiores. Elvalor mínimo especificado es en ese caso proporcional al área transversal de la probeta (muestra) en comparación con una probeta de tamaño estándar (10 x 10 mm).

             

             

             

            Ultrasonic testing

            Ultrasonic inspection is carried out according to : EN 10 160 with extra demands according to specification SSAB V6.

            Tolerancias

            More details are given in SSAB’s brochure Toolox® Guarantees and on www.toolox.com.

            Espesor

            Tolerances according to Toolox® Thickness Guarantee.

            Toolox® Guarantees meets the requirements of EN 10029 Class C but offers more narrow tolerances.

            Largo y ancho

            Tolerances according to EN 10029.

            Planitud

            Tolerances are according to Toolox® Flatness Guarantees, which are more restrictive than EN 10029 Class N (steel type L).

            Propiedades superficiales

            De conformidad con la norma EN 10163-2, clase B, subclase 3.

            Condiciones de entrega

            Quenched and Tempered at a minimum temperature of 590 °C.

            On delivery from SSAB the plates meet the following specifications:

            • Free from mill scale
            • Not repair welded

            Delivery requirements can be found in SSAB’s brochure Toolox® Guarantees or at www.toolox.com.