Hardox® HiAce korkeisiin lämpötiloihin
Hardox® HiAce on korroosionkestävä ja kuumuutta kestävä Hardox®-kulutuslevy. Se on kustannustehokas ratkaisu, joka tarjoaa kulutuskestävyyttä korkeissa lämpötiloissa, vähintään 400 °C:seen asti Sen nimelliskovuus on 400 HBW. Tavanomaiset karkaistut ja nuorrutetut teräkset menettävät kovuuttaan korkeissa lämpötiloissa, mutta Hardox® HiAce -teräs säilyttää kovuutensa ja kulutuskestävyytensä.
A high-temp metal that resists abrasion and corrosion
Many industrial applications combine three major challenges: abrasive materials, elevated temperatures and corrosive environments. Hardox® HiAce steel is specifically designed to handle this demanding combination.
If you need to build heavy equipment that has to resist wear while operating at high temperatures, Hardox® HiAce provides a durable solution. While traditional quenched and tempered steels experience significant hardness loss at temperatures of 300-500 °C (about 570-930 °F), this high temp metal maintains its strength and hardness to help extend the service life of costly equipment.
At the same time, Hardox® HiAce offers corrosion resistance that helps protect components exposed to aggressive process environments. This makes it ideal for applications where hot materials, wear and chemical attack occur at the same time.
The outstanding performance of this heat-resistant steel is achieved through high-quality raw materials combined with a carefully controlled manufacturing process. And in your workshop, Hardox® HiAce can be cut, welded, machined and cold formed using the same equipment as other Hardox® grades and conventional AR steel.
A heat resistant steel for a wide variety of uses
Abrasive and hot materials – such as asphalt, foundry sand and cement clinker – place extreme demands on industrial equipment and truck bodies. In truck bodies that handle hot bulk materials, Hardox® HiAce allows for thinner plates in the floor and sides, which increases payload capacity while maintaining durability. Plus, the reduced weight also lowers the overall weight of the truck when travelling empty.
In coking plant equipment, Hardox® HiAce provides a cost-effective, long-lasting steel solution in:
- Coke ramps
- Quenching wagons
- Cooling beds
- Tippers
- Furnace inlet scrapers
- Other heat-affected equipment in process industries.
In short, Hardox® HiAce makes a strong choice wherever high wear resistance and structural strength are needed in high-temperature environments.
Get free technical adviceHardox® HiAce reduces maintenance intervals from months to years at coke plant
When red-hot coke from furnaces is discharged onto sliding ramps, the ramp liners face extremely demanding conditions. In addition to high temperatures and heavy abrasion, coke can also be mildly to moderately corrosive.
By replacing thick ceramic tiles – which are expensive and prone to cracking – with steel plates made from Hardox® HiAce, SSAB’s plant in Sweden was able to drastically reduce maintenance requirements while improving operational safety.
The result: lower maintenance costs, fewer shutdowns and a safer working environment.
The high-temp steel for demanding industrial applications
Hardox® HiAce is well suited for applications involving moderate abrasive wear, high temperatures and corrosive conditions, especially in industries like steel, cement, asphalt, power generation and recycling.
Typical applications for this high temp steel include:
- Dryer drums and lifter plates inside dryers in asphalt plants
- Clinker cooler plates and other liner plates in cement plants
- Blast furnace components and slag buckets in steel plants
- Rotary seal valves in coke plants
- Ash handling equipment and chain conveyers in power plants
- Scrapers, screeners and liner plates in foundries
- Liner plates, crusher hammers for gypsum and clinker
Heat-resistant ceramics vs. our high-temperature steel
In some high-temperature environments, materials like ceramics or mild steel are used to resist wear. But these solutions often come with limitations.
For example, coke ramps made in thick basalt ceramic tiles can be incredibly expensive and are prone to cracking. This leads to frequent maintenance stops and money-wasting downtime.
Hardox® HiAce offers a durable alternative. It provides high wear resistance, good structural strength and lower weight, while also being easier to fabricate and install. Because of its workshop-friendly properties, you can cut, weld and form it using conventional equipment, making installation faster and more efficient than many ceramic solutions.
Benefits of Hardox® HiAce heat-resistant steel
- Corrosion-resistance helps extend service life in aggressive environments and reduce maintenance requirements
- High toughness makes it suitable for rapid temperatures changes or freezing conditions without cracking
- Resists deformation, buckling and cracking at elevated temperatures
- Allows thinner plates for lower equipment weight, higher payload capacity and prolonged service life
- Easily cold formed using conventional methods
- Helps reduce maintenance, downtime and operating costs while improving safety
- Can be cut, welded and machined using the same equipment as other Hardox® grades and conventional AR steel.
Made for predictable workshop performance
Welding
Hardox® wear plate combines exceptional performance with excellent weldability. Conventional welding methods can be used to weld to other weldable steels. Our welding recommendations cover heat input, preheating, input, preheating, consumables and procedures for reliable welds and optimal steel performance.
Welding recommendations for Hardox® HiAce
Drilling and machining
Hardox® wear plate can be machined using high-speed steel (HSS) or cemented carbide (CC) tools. Our machining guide provides recommended tooling, cutting data (feeds and speeds) and practical tips to help you achieve efficient machining and good tool life.
Drilling and machining guidelines for Hardox® HiAce
Bending
Hardox® wear plate combines high strength with reliable formability. Our bending guide includes practical recommendations for achieving the best results when bending, including on plate thickness, steel grade, and bending direction relative to the rolling direction. This helps ensure consistent press-brake performance.
Bending recommendations for Hardox® HiAce
Cutting
Hardox® wear plate can be cut using both thermal methods (plasma, laser, oxy-fuel) and cold-cutting methods (abrasive waterjet, sawing). Our cutting recommendations help you select the right cutting method and parameters to achieve clean cut edges and stable production.
Cutting Hardox® HiAce
Hardox® guarantees
Hardox® guarantees include tight thickness tolerances, tight flatness tolerances, and tight bending guarantees. These guarantees complement the Hardox® datasheets and reinforce our commitment to predictable workshop performance.
Review the Hardox® Guarantees
Tech support
Hardox® steel is more than a wear plate – it comes with the technical expertise to help you get the most out of it. Our specialists provide practical guidance on welding, bending, drilling and machining so you can fabricate with confidence from workshop to final application.
Contact technical support
Did you know?
Hardox® HiAce is also the best steel against corrosive wear
Discover moreMittavalikoima
Hardox® HiAce -levyjä on saatavina 4.0 - 100.0 mm paksuina ja Hardox® HiAce -nauhalevyjä 3.0 - 4.0 mm paksuina. Hardox® HiAce -levyjä on saatavina 3350 mm:n leveyteen ja 14630 mm:n pituuteen asti. Hardox® HiAce -nauhalevyjä on saatavina 1600 mm:n leveyteen ja 16000 mm:n pituuteen asti. Tarkempia tietoja mitoista saa mittaohjelmasta.
Mekaaniset ominaisuudet
(mmin)
(HBW)
(MPaksi), ei taattu
(mmin)
(HBW)
(MPaksi), ei taattu
1) Brinell-kovuustesti, HBW, EN ISO 6506-1 -standardin mukaisesti, koneistetulta pinnalta 0.5–3.0 mm pinnan alapuolella. Vähintään yksi testinäyte sulatusta ja 40 tonnia kohden. Toimitettujen levyjen nimellispaksuus ei poikkea yli ± 15 mm kovuuskokeen testinäytteestä. Nauhalevy Brinell-kovuustesti on EN ISO 6506-1 -standardin mukainen jokaisessa lämpökäsittelyyksikössä / kelassa. Kovuus mitataan jauhamalla pinta 0.3 - 2.0 mm pinnan alapuolella.
Hardox® -levy on läpikova. Paksuussuuntaisen keskialueen kovuus on vähintään 90 % taatusta kovuudesta.
Iskusitkeysominaisuudet
(mmin)
(mmin)
1) Iskukokeet tehdään ≥ 6 mm:n paksuuksille levyja ≥ 3 nauhalevyillä:n paksuuksille. Paksuuksille 3 – 11,9 mm käytetään alimittaisia Charpy V -iskusauvoja. Ilmoitettu vähimmäisarvo koskee iskusauvan poikkileikkausalaa suhteessa täysimittaiseen iskusauvaan (10 x 10 mm). Iskukokeet tehdään standardin ISO EN 148 mukaisesti sulatus- ja paksuusryhmäkohtaisesti. Kolmen testituloksen keskiarvo.
2) Yksittäinen arvo vähintään 70 % ilmoitetusta keskiarvosta.
Kemiallinen koostumus (sulatusanalyysi)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
(max %)
Teräs on hienoraekäsitelty *) Varsinaiset seosaineet.
Hiiliekvivalentti CET(CEV)
Paksuus
Toleranssit ovat Hardox®-paksuustakuiden mukaisia.
Hardox®-takuut täyttävät EN 10029:n luokan A vaatimukset, mutta tiukemmilla toleransseilla. Nauhalevy takuut täyttävät standardin 1/2 EN 10051 vaatimukset.
Pituus ja leveys
SSAB:n mittaohjelman mukaisesti. Levyjen toleranssit ovat SSAB:n valssausreunastandardien mukaisia tai täyttävät standardin EN 10 029 vaatimukset. Nauhalevyjen toleranssit täyttävät standardin EN 10 051 vaatimukset, ja tiukempia toleransseja on saatavana erikseen kysyttäessä.
Muoto
Levyjen toleranssit ovat standardin EN 10029 mukaisia ja nauhalevyjen toleranssit standardin EN 10051 mukaisia.
Tasomaisuus
Hardox® tasomaisuustakuun C-luokan mukaiset levytoleranssit ovat tiukemmat kuin EN 10029 luokan N vaatimukset. Ohuilla levyillä toleranssit noudattavat Hardox® tasomaisuustakuun A-luokkaa, joka on tarkempi kuin EN 10051.
Pinnanlaatu
EN 10163-2:n luokan A alaluokan 1 mukaisesti.
Toimitustila
Toimitustila on karkaistu tai nuorrutettu. Hardox® -levyt toimitetaan mekaanisesti tai termisesti leikatuin reunoin, ja yli 80 mm:n paksuudet toimitetaan tavallisesti valssausreunoin. Hardox® -nauhalevyt toimitetaan tavallisesti valssatulla pinnalla ja valssausreunoilla.
Toimitusehdot on kuvattu SSAB:n esitteessä "Hardox® Guarantees" ja osoitteessa www.ssab.com.
Valmistus- ja muut suositukset
Hitsaaminen, taivuttaminen ja koneistaminen
Suosituksia löytyy SSAB:n esitteistä osoitteesta www.hardox.com tai ottamalla yhteyttä ottamalla yhteyttä tekniseen tukeen.
Levyjen taivutettavuus on Hardox® -taivutustakuiden luokan E mukainen. Nauhalevyjen taivutettavuus on Hardox® -taivutustakuiden luokan A mukainen.
Hardox® HiAce säilyttää usein ≥90 % taatusta minimikovuudesta altistuessaan jopa 400 °C lämpötiloille. Huomioithan, että altistuminen korkeille lämpötiloille tämän rajan ylä- ja alapuolella voi heikentää mekaanisia ominaisuuksia ajan myötä. Toimitustilan säilymistä ei voida taata. Ota yhteyttä SSAB:hen lisäkeskustelua varten.
Kun tuotetta hitsataan, leikataan, hiotaan tai työstetään muulla tavoin, on noudatettava asianmukaisia työturvallisuusohjeita. Erityisesti pohjamaalattuja levyjä hiottaessa saattaa muodostua pölyä, jonka hiukkaspitoisuus on suuri.