Docol® S600MC high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

General Product Description

The high-strength structural steel Docol S600MC is a hot-rolled steel made for cold forming, with a minimum yield strength of 600 MPa for stronger and lighter structures. Docol S600MC meets or exceeds the requirements of S600MC in EN 10149-2. Typical applications include a wide range of heavy trucks components and parts, such as frame rails and cross-members. Docol S600MC comes in coils, slit coils and cut-to-length sheets.

Dimension Range

Hot rolled / UC: thickness 2.00-10.00 mm, width up to 1600 mm.

Slit strip and cut to length sheets are available upon request.

Mechanical Properties

Thickness (mmin)	Standard	Coating	Test direction	Yield strength R_eH¹⁾ (min MPaksi)	Tensile strength R_m (MPaksi)	Elongation A₈₀²⁾ (min %)	Elongation A₅³⁾ (min %)	Min. inner bending radius for a 90° bend⁴⁾ (x t)
2.00 - 3.000.079 - 0.118	SSAB	UC	L	60087	650 - 82094 - 119	13	16	0.7
3.01 - 6.000.119 - 0.236	SSAB	UC	L	60087	650 - 82094 - 119	—	16	1.1
6.01 - 10.000.237 - 0.393	SSAB	UC	L	60087	650 - 82094 - 119	—	16	1.4

Thickness
(mmin)

2.00 - 3.000.079 - 0.118

Standard

SSAB

Coating

Test direction

Yield strength R_eH¹⁾
(min MPaksi)

60087

Tensile strength R_m
(MPaksi)

650 - 82094 - 119

Elongation A₈₀²⁾
(min %)

Elongation A₅³⁾
(min %)

Min. inner bending radius for a 90° bend⁴⁾
(x t)

0.7

Thickness
(mmin)

3.01 - 6.000.119 - 0.236

Standard

SSAB

Coating

Test direction

Yield strength R_eH¹⁾
(min MPaksi)

60087

Tensile strength R_m
(MPaksi)

650 - 82094 - 119

Elongation A₈₀²⁾
(min %)

—

Elongation A₅³⁾
(min %)

Min. inner bending radius for a 90° bend⁴⁾
(x t)

1.1

Thickness
(mmin)

6.01 - 10.000.237 - 0.393

Standard

SSAB

Coating

Test direction

Yield strength R_eH¹⁾
(min MPaksi)

60087

Tensile strength R_m
(MPaksi)

650 - 82094 - 119

Elongation A₈₀²⁾
(min %)

—

Elongation A₅³⁾
(min %)

Min. inner bending radius for a 90° bend⁴⁾
(x t)

1.4

¹⁾ If R_eH is not applicable then Rp_0.2 is used.

²⁾ A₈₀ value applies for thicknesses < 3.00 mm.

³⁾ A₅ value applies for thicknesses ≥ 3.00 mm.

⁴⁾ For both longitudinal and transverse direction.

Impact Properties

Product	Min. impact energy for longitudinal testing, Charpy V 10x10 mm test specimen
Docol S600MC D	40 J / -20 °C29 ft-lbs / -4 °F
Docol S600MC E	27 J / -40 °C20 ft-lbs / -40 °F

Product

Docol S600MC D

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimen

40 J / -20 °C29 ft-lbs / -4 °F

Product

Docol S600MC E

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimen

27 J / -40 °C20 ft-lbs / -40 °F

Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 6mm. The specified minimum value corresponds to a full-size specimen.

Chemical Composition (heat analysis)

C (max %)	Si (max %)	Mn (max %)	P (max %)	S (max %)	Nb (max %)	V (max %)	Ti (max %)
0.12	0.21 ¹⁾	1.90	0.025	0.010	0.09 ²⁾	0.20 ²⁾	0.15 ²⁾

C
(max %)

0.12

Si
(max %)

0.21 ¹⁾

Mn
(max %)

1.90

P
(max %)

0.025

S
(max %)

0.010

Nb
(max %)

0.09 ²⁾

V
(max %)

0.20 ²⁾

Ti
(max %)

0.15 ²⁾

¹⁾ If the material is to be hot-dip galvanized, this must be specified in the order. Galvanizing class A available upon request.

²⁾ Sum of Nb, V and Ti = max 0.22%.

The steel is grain refined.

Carbon Equivalent CET(CEV)

Thickness (mmin)	2.00 - 10.000.079 - 0.393
Typ CET(CEV)	0.21 (0.33)

Thickness (mmin)

Typ CET(CEV)

2.00 - 10.000.079 - 0.393

0.21 (0.33)

Tolerances

Hot rolled (UC): Tolerances in accordance to EN 10051.

Customized dimensional and shape tolerances are available upon request.

Surface Treatments

Uncoated (UC): available as black or pickled and oiled.

All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr⁶⁺). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

Fabrication and Other Recommendations

For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

Docol® High Strength Low Alloy steel product offer

Contenuti correlati

Stock di materiale di prova

Vuoi scoprire applicazioni automotive uniche nel loro genere, sperimentare nuovi metodi di produzione o creare componenti più leggeri che possano migliorare l'efficienza del carburante, la resistenza all'impatto dei veicoli e la sostenibilità?

Dati di formatura per gli acciai AHSS Docol®

Gli attuali clienti Docol® hanno accesso 24 ore su 24, 7 giorni su 7 ai dati di formatura necessari per aiutarli nella scelta e nella simulazione degli acciai altoresistenziali di nuova generazione per il settore automobilistico.

General Product Description

Dimension Range

Mechanical Properties

Impact Properties

Chemical Composition (heat analysis)

Carbon Equivalent CET(CEV)

Tolerances

Surface Treatments

Fabrication and Other Recommendations