Docol® 800DH dual phase with high formability
More about dual phase with high formability steelDownload data sheet
Download data sheet
Docol 800DH trip assisted dual-phase steels provide improved formability and weldability and are suitable for car safety and structural components.
This steel undergoes a special heat treatment producing mainly two-phase structure. Ferrite that imparts unique forming properties represents one phase and martensite that accounts for the strength represents the other phase. Small amount of bainite and retained austenite improves formability further.
Cold rolled / GI: thickness 0.80-2.40 mm, width up to 1400 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
n4-6 (min) |
n10-20/Ag (min) |
BH2 (min MPa) |
|
---|---|---|---|---|---|---|---|---|---|
Docol CR440Y780T-DH | VDA 239-100 | GI | L | 440 - 550 | 780 - 900 | 18 | 0.18 | 0.13 | 30 |
Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
---|---|---|---|---|---|---|---|---|---|---|---|
Docol CR440Y780T-DH | GI | 0.18 | 0.80 | 2.50 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 |
Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Coating type | Coating class | Standard | Closest in EN 10346, informative | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) | Density (g/cm3) | Surface quality (U = unexposed, E = exposed) |
---|---|---|---|---|---|---|---|
GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 1) | 5.6 - 8.5 | 7.1 | U |
GI | 50/50 | VDA 239-100 | — | 50 - 70 1) | 7.0 - 9.9 | 7.1 | U |
GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 | 7.1 | U |
GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 | 7.1 | U |
GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 | 7.1 | U |
GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 | 7.1 | U |
In addition to these coating masses, asymmetric coatings and OEM coating specifications are available upon request.
1) For hot-dipped (GI, ZA, GA) hot rolled (HR) grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.
Hot-dip galvanized (GI): available as oiled and/or chemically passivated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Vuoi scoprire applicazioni automotive uniche nel loro genere, sperimentare nuovi metodi di produzione o creare componenti più leggeri che possano migliorare l'efficienza del carburante, la resistenza all'impatto dei veicoli e la sostenibilità?
Gli attuali clienti Docol® hanno accesso 24 ore su 24, 7 giorni su 7 ai dati di formatura necessari per aiutarli nella scelta e nella simulazione degli acciai altoresistenziali di nuova generazione per il settore automobilistico.