Docol® 800CP complex phase
More about complex phase steelDownload data sheet
Download data sheet
Docol 800CP is intended for designs where high structural strength and energy absorption are desired, suitable for cold formed safety components and crash-relevant equipment within the automotive and transport industries.
Cold rolled / UC: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI, GA, ZA: thickness 0.80-2.50 mm, width up to 1460 mm.
Hot rolled / UC: thickness 2.00-4.00 mm, width up to 1500 mm.
Hot rolled / GI: thickness 2.00-3.50 mm, width up to 1400 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
Elongation A5 (min %) |
BH2 (min MPa) |
Hole expansion ratio 2)(min %) | Hole expansion ratio 2) (% typical) |
|
---|---|---|---|---|---|---|---|---|---|---|
Docol CR570Y780T-CP | VDA 239-100 | UC, GI, GA*, ZA* | L | 570 - 720 | 780 - 920 | 10 1) | — | 30 | — | — |
Docol HR660Y760T-CP | VDA 239-100 | UC, GI | L | 660 - 820 | 760 - 960 | 10 | 13 | 30 | — | — |
Docol HR800HER-75 | SSAB | UC, GI | L | 660 - 820 | 760 - 960 | 11 | 14 | 30 | 45 | 75 |
Docol HR800HER-100 | SSAB | UC | L | 660 - 820 | 760 - 960 | 12 | 15 | 30 | 65 | 100 |
Docol Roll 800 | SSAB | UC | T | 600 - 750 | 800 - 950 | 10 | — | — | — | — |
*Available upon request.
1) For GA coatings the minimum elongation value is reduced by 2 units.
2) HER –ratio is average of three test results out of five tested samples by excluding minimum and maximum results.
Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
---|---|---|---|---|---|---|---|---|---|---|---|
Docol CR570Y780T-CP | UC, GI, GA*, ZA* | 0.18 | 1.00 | 2.50 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.00 | 0.005 | 0.20 |
Docol HR660Y760T-CP | UC, GI | 0.18 | 1.00 | 2.20 | 0.050 | 0.010 | 0.015 - 1.2 | 0.25 | 1.00 | 0.005 | 0.20 |
Docol HR800HER-75 | UC, GI | 0.18 | 1.00 | 2.20 | 0.050 | 0.010 | 0.015 - 1.2 | 0.25 | 1.00 | 0.005 | 0.20 |
Docol HR800HER-100 | UC | 0.18 | 1.00 | 2.20 | 0.050 | 0.010 | 0.015 - 1.2 | 0.25 | 1.00 | 0.005 | 0.20 |
Docol Roll 800 | UC | 0.16 | 0.40 | 1.80 | 0.020 | 0.010 | From 0.015 | 0.10 | — | — | — |
Cold rolled (UC): Tolerances in accordance to EN 10131.
Hot rolled (UC): Tolerances in accordance to EN 10051.
Hot-dip galvanized (GI, GA, ZA): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.
Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Coating type | Coating class | Standard | Closest in EN 10346, informative | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) |
---|---|---|---|---|---|
GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 1) | 5.6 - 8.5 |
GI | 50/50 | VDA 239-100 | — | 50 - 70 1) | 7.0 - 9.9 |
GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 |
GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 |
GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 |
GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 |
GA | 40/40 | VDA 239-100 | ZF100 | 40 - 60 1) | 5.6 - 8.5 |
GA | 50/50 | VDA 239-100 | ZF120 | 50 - 80 | 7.0 - 11.3 |
ZA | 95 | EN 10346 | ZA95 | — | 7.0 - |
ZA | 130 | EN 10346 | ZA130 | — | 10.0 - |
EG | 25/25 | EN 10152 | — | 12 - | 1.7 - |
EG | 50/50 | EN 10152 | — | 29 - | 4.1 - |
EG | 75/75 | EN 10152 | — | 47 - | 6.6 - |
EG | 100/100 | EN 10152 | — | 65 - | 9.1 - |
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For hot-dipped (GI, ZA, GA) hot rolled (HR) grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI, GA, ZA): available as oiled and/or chemically passivated.
Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.