Docol® 1000DP dual phase
More about dual phase steelDownload data sheet
Download data sheet
Developed for increased safety in cars. Docol 1000DP steels have excellent forming and welding properties. These steels undergo special heat treatment, producing mainly two phase structure. Ferrite that imparts unique forming properties represents one phase, and martensite that accounts for the strength represents the other phase. Bainite may be present as complementary phase.
Cold rolled / UC, EG: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI, GA, ZA: thickness 0.80-2.00 mm, width up to 1460 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
BH2 (min MPa) |
Min. inner bending radius for a 90° bend 3) | |
---|---|---|---|---|---|---|---|---|
Docol CR590Y980T DP | VDA 239-100 | UC, EG | L | 590 - 740 | 980 - 1130 | 10 | 30 | 2.0 x t |
VDA 239-100 | GI, GA, ZA | L | 590 - 740 | 980 - 1130 | 10 1) | 30 | 3.0 x t | |
Docol CR700Y980T DP | VDA 239-100 | UC, EG | L | 700 - 850 | 980 - 1130 | 8 | 30 | 2.0 x t |
VDA 239-100 | GI, GA*, ZA* | L | 700 - 850 | 980 - 1130 | 8 1) | 30 | 3.0 x t | |
Docol CR700Y980T DP LCE | SSAB | UC, EG | L | 700 - 900 | 980 - 1130 | 8 | — | 2.0 x t |
VDA 239-100 | GI, GA*, ZA* | L | 700 - 850 | 980 - 1130 | 8 1) | 30 | 2.5 x t | |
Docol CR700Y1000T DP | SSAB | UC, EG | T | 700 - 950 | 1000 - 1200 | 7 2) | — | 2.0 x t |
Docol 1000DPX | VDA 239-100 | GI, GA* | T | 800 - 1000 | 1000 - 1200 | 6 | 30 | 2.5 x t |
The testing of mechanical properties of electro galvanized products is conducted without coating.
* Available upon request.
1) For GA coatings the minimum elongation value is reduced by 2 units.
2) Decreased minimum elongation values apply for product thickness t < 0.70 mm (minus 2 units).
3) In some cases tight bending radius may cause micro-cracking of the coating in the bend area. Where design permits, users are encouraged to employ larger radius.
Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
---|---|---|---|---|---|---|---|---|---|---|---|
Docol CR590Y980T DP | UC, EG | 0.18 | 0.60 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 1.40 | 0.005 | 0.20 |
GI, GA, ZA | 0.20 | 1.00 | 2.90 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
Docol CR700Y980T DP | UC, EG | 0.16 | 0.40 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 0.15 | 0.005 | 0.20 |
GI, GA*, ZA* | 0.23 | 1.00 | 2.90 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
Docol CR700Y980T DP LCE | UC, EG | 0.16 | 0.40 | 2.60 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 0.15 | 0.005 | 0.20 |
GI, GA*, ZA* | 0.15 | 0.8 | 2.90 | 0.020 | 0.005 | 0.01 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
Docol CR700Y1000T DP | UC, EG | 0.18 | 0.80 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 1.40 | 0.005 | 0.20 |
Docol 1000DPX | GI, GA* | 0.23 | 1.00 | 2.70 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.00 | 0.005 | 0.20 |
Cold rolled (UC, EG): Tolerances in accordance to EN 10131.
Hot-dip galvanized (GI, GA, ZA): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.
Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Coating type | Coating class | Standard | Closest in EN standard, informative 1) | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) |
---|---|---|---|---|---|
GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 | 5.6 - 8.5 |
GI | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 |
GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 |
GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 |
GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 |
GA | 40/40 | VDA 239-100 | ZF100 | 40 - 60 | 5.6 - 8.5 |
GA | 50/50 | VDA 239-100 | ZF120 | 50 - 80 | 7.0 - 11.3 |
ZA | 95 | EN 10346 | ZA95 | — | 7.0 - |
ZA | 130 | EN 10346 | ZA130 | — | 10.0 - |
EG | 12/12 | VDA 239-100 | ZE25/25 | 12 - 32 | 1.7 - 4.5 |
EG | 18/18 | VDA 239-100 | — | 18 - 38 | 2.5 - 5.4 |
EG | 29/29 | VDA 239-100 | ZE50/50 | 29 - 49 | 4.1 - 6.9 |
EG | 47/47 | VDA 239-100 | ZE75/75 | 47 - 61 | 6.6 - 8.6 |
EG | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
EG | 53/53 | VDA 239-100 | — | 53 - 73 | 7.5 - 10.3 |
EG | 60/60 | VDA 239-100 | — | 60 - 80 | 8.5 - 11.3 |
EG | 65/65 | VDA 239-100 | ZE100/100 | 65 - 85 | 9.2 - 12.0 |
EG | 70/70 | VDA 239-100 | — | 70 - 90 | 9.9 - 12.7 |
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For GI and GA the closest informative value refers to EN 10346. For EG to EN 10152.
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI, GA, ZA): available as oiled and/or chemically passivated.
Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Want to discover unique automotive applications for AHSS materials? Try new production methods? Or create lighter components that can improve fuel efficiency, crash-worthiness and sustainability?
Docol® steel grades serve specific design purposes and are chosen by designers for a wide range of applications and used by OEMs and tier suppliers in millions of vehicles around the world.
Existing Docol® customers get 24/7 access to the forming data you need to help in your selection and simulation of automotive advanced high strength steels.