General Product Description
Developed for increased safety in cars. Docol 1000DP steels have excellent forming and welding properties. These steels undergo special heat treatment, producing mainly two phase structure. Ferrite that imparts unique forming properties represents one phase, and martensite that accounts for the strength represents the other phase. Bainite may be present as complementary phase.
Dimension Range
Cold rolled / UC, EG: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI, GA, ZA: thickness 0.80-2.00 mm, width up to 1460 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Mechanical Properties
Hide/Show specific columns Edit
Select columns to display
| Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
BH2 (min MPa) |
Min. inner bending radius for a 90° bend 3) | |
|---|---|---|---|---|---|---|---|---|
| Docol CR590Y980T-DP | VDA 239-100 | UC, EG | L | 590 - 740 | 980 - 1130 | 10 | 30 | 2.0 x t |
| VDA 239-100 | GI, GA, ZA | L | 590 - 740 | 980 - 1130 | 10 1) | 30 | 3.0 x t | |
| Docol CR700Y980T-DP | VDA 239-100 | UC, EG | L | 700 - 850 | 980 - 1130 | 8 | 30 | 2.0 x t |
| VDA 239-100 | GI, GA*, ZA* | L | 700 - 850 | 980 - 1130 | 8 1) | 30 | 3.0 x t | |
| Docol CR700Y980T-DP-LCE | SSAB | UC, EG | L | 700 - 900 | 980 - 1130 | 8 | — | 2.0 x t |
| VDA 239-100 | GI, GA*, ZA* | L | 700 - 850 | 980 - 1130 | 8 1) | 30 | 2.5 x t | |
| Docol CR700Y1000T-DP | SSAB | UC, EG | T | 700 - 950 | 1000 - 1200 | 7 2) | — | 2.0 x t |
| Docol 1000DPX | VDA 239-100 | GI, GA* | T | 800 - 1000 | 1000 - 1200 | 6 | 30 | 2.5 x t |
Compare parameters
Select one parameter to compare
Comparison
Docol CR590Y980T-DP
Standard
VDA 239-100
Coating
UC, EG
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
590 - 740
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
10
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
2.0 x t
Expand
Collapse
Docol CR590Y980T-DP
Standard
VDA 239-100
Coating
GI, GA, ZA
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
590 - 740
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
10 1)
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
3.0 x t
Expand
Collapse
Docol CR700Y980T-DP
Standard
VDA 239-100
Coating
UC, EG
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
700 - 850
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
8
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
2.0 x t
Expand
Collapse
Docol CR700Y980T-DP
Standard
VDA 239-100
Coating
GI, GA*, ZA*
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
700 - 850
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
8 1)
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
3.0 x t
Expand
Collapse
Docol CR700Y980T-DP-LCE
Standard
SSAB
Coating
UC, EG
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
700 - 900
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
8
BH2
(min MPa)
(min MPa)
—
Min. inner bending radius for a 90° bend 3)
2.0 x t
Expand
Collapse
Docol CR700Y980T-DP-LCE
Standard
VDA 239-100
Coating
GI, GA*, ZA*
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
700 - 850
Tensile strength Rm
(MPa)
(MPa)
980 - 1130
Elongation A80
(min %)
(min %)
8 1)
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
2.5 x t
Expand
Collapse
Docol CR700Y1000T-DP
Standard
SSAB
Coating
UC, EG
Test direction
T
Yield strength Rp0.2
(MPa)
(MPa)
700 - 950
Tensile strength Rm
(MPa)
(MPa)
1000 - 1200
Elongation A80
(min %)
(min %)
7 2)
BH2
(min MPa)
(min MPa)
—
Min. inner bending radius for a 90° bend 3)
2.0 x t
Expand
Collapse
Docol 1000DPX
Standard
VDA 239-100
Coating
GI, GA*
Test direction
T
Yield strength Rp0.2
(MPa)
(MPa)
800 - 1000
Tensile strength Rm
(MPa)
(MPa)
1000 - 1200
Elongation A80
(min %)
(min %)
6
BH2
(min MPa)
(min MPa)
30
Min. inner bending radius for a 90° bend 3)
2.5 x t
Expand
Collapse
The testing of mechanical properties of electro galvanized products is conducted without coating.
* Available upon request.
1) For GA coatings the minimum elongation value is reduced by 2 units.
2) Decreased minimum elongation values apply for product thickness t < 0.70 mm (minus 2 units).
3) In some cases tight bending radius may cause micro-cracking of the coating in the bend area. Where design permits, users are encouraged to employ larger radius.
Chemical Composition (ladle analysis)
Hide/Show specific columns Edit
Select columns to display
| Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
|---|---|---|---|---|---|---|---|---|---|---|---|
| Docol CR590Y980T-DP | UC, EG | 0.18 | 0.60 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 1.40 | 0.005 | 0.20 |
| GI, GA, ZA | 0.20 | 1.00 | 2.90 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
| Docol CR700Y980T-DP | UC, EG | 0.16 | 0.40 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 0.15 | 0.005 | 0.20 |
| GI, GA*, ZA* | 0.23 | 1.00 | 2.90 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
| Docol CR700Y980T-DP-LCE | UC, EG | 0.16 | 0.40 | 2.60 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 0.15 | 0.005 | 0.20 |
| GI, GA*, ZA* | 0.15 | 0.8 | 2.90 | 0.020 | 0.005 | 0.01 - 1.00 | 0.15 | 1.40 | 0.005 | 0.20 | |
| Docol CR700Y1000T-DP | UC, EG | 0.18 | 0.80 | 1.80 | 0.020 | 0.010 | 0.015 - 1.00 | 0.10 | 1.40 | 0.005 | 0.20 |
| Docol 1000DPX | GI, GA* | 0.23 | 1.00 | 2.70 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.00 | 0.005 | 0.20 |
Compare parameters
Select one parameter to compare
Comparison
Docol CR590Y980T-DP
Coating
UC, EG
C
(max %)
(max %)
0.18
Si
(max %)
(max %)
0.60
Mn
(max %)
(max %)
1.80
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR590Y980T-DP
Coating
GI, GA, ZA
C
(max %)
(max %)
0.20
Si
(max %)
(max %)
1.00
Mn
(max %)
(max %)
2.90
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR700Y980T-DP
Coating
UC, EG
C
(max %)
(max %)
0.16
Si
(max %)
(max %)
0.40
Mn
(max %)
(max %)
1.80
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
0.15
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR700Y980T-DP
Coating
GI, GA*, ZA*
C
(max %)
(max %)
0.23
Si
(max %)
(max %)
1.00
Mn
(max %)
(max %)
2.90
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR700Y980T-DP-LCE
Coating
UC, EG
C
(max %)
(max %)
0.16
Si
(max %)
(max %)
0.40
Mn
(max %)
(max %)
2.60
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
0.15
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR700Y980T-DP-LCE
Coating
GI, GA*, ZA*
C
(max %)
(max %)
0.15
Si
(max %)
(max %)
0.8
Mn
(max %)
(max %)
2.90
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.005
Al
(%)
(%)
0.01 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol CR700Y1000T-DP
Coating
UC, EG
C
(max %)
(max %)
0.18
Si
(max %)
(max %)
0.80
Mn
(max %)
(max %)
1.80
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
1.40
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol 1000DPX
Coating
GI, GA*
C
(max %)
(max %)
0.23
Si
(max %)
(max %)
1.00
Mn
(max %)
(max %)
2.70
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.00
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
* Available upon request.
Tolerances
Cold rolled (UC, EG): Tolerances in accordance to EN 10131.
Hot-dip galvanized (GI, GA, ZA): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
Coatings
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.
Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Hide/Show specific columns Edit
Select columns to display
| Coating type | Coating class | Standard | Closest in EN standard, informative 1) | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) |
|---|---|---|---|---|---|
| GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 | 5.6 - 8.5 |
| GI | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
| GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 |
| GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 |
| GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 |
| GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 |
| GA | 40/40 | VDA 239-100 | ZF100 | 40 - 60 | 5.6 - 8.5 |
| GA | 50/50 | VDA 239-100 | ZF120 | 50 - 80 | 7.0 - 11.3 |
| ZA | 95 | EN 10346 | ZA95 | — | 7.0 - |
| ZA | 130 | EN 10346 | ZA130 | — | 10.0 - |
| EG | 12/12 | VDA 239-100 | ZE25/25 | 12 - 32 | 1.7 - 4.5 |
| EG | 18/18 | VDA 239-100 | — | 18 - 38 | 2.5 - 5.4 |
| EG | 29/29 | VDA 239-100 | ZE50/50 | 29 - 49 | 4.1 - 6.9 |
| EG | 47/47 | VDA 239-100 | ZE75/75 | 47 - 61 | 6.6 - 8.6 |
| EG | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
| EG | 53/53 | VDA 239-100 | — | 53 - 73 | 7.5 - 10.3 |
| EG | 60/60 | VDA 239-100 | — | 60 - 80 | 8.5 - 11.3 |
| EG | 65/65 | VDA 239-100 | ZE100/100 | 65 - 85 | 9.2 - 12.0 |
| EG | 70/70 | VDA 239-100 | — | 70 - 90 | 9.9 - 12.7 |
Compare parameters
Select one parameter to compare
Comparison
Coating type
GI
Coating class
40/40
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z100
Coating mass per side, single spot test (g/m2)
40 - 60
Thickness per side informative (µm)
5.6 - 8.5
Expand
Collapse
Coating type
GI
Coating class
50/50
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
50 - 70
Thickness per side informative (µm)
7.0 - 9.9
Expand
Collapse
Coating type
GI
Coating class
60/60
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z140
Coating mass per side, single spot test (g/m2)
60 - 90
Thickness per side informative (µm)
8.5 - 12.7
Expand
Collapse
Coating type
GI
Coating class
70/70
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
70 - 100
Thickness per side informative (µm)
9.9 - 14.1
Expand
Collapse
Coating type
GI
Coating class
85/85
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
85 - 115
Thickness per side informative (µm)
12.0 - 16.2
Expand
Collapse
Coating type
GI
Coating class
115/115
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z275
Coating mass per side, single spot test (g/m2)
115 - 155
Thickness per side informative (µm)
16.2 - 21.8
Expand
Collapse
Coating type
GA
Coating class
40/40
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZF100
Coating mass per side, single spot test (g/m2)
40 - 60
Thickness per side informative (µm)
5.6 - 8.5
Expand
Collapse
Coating type
GA
Coating class
50/50
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZF120
Coating mass per side, single spot test (g/m2)
50 - 80
Thickness per side informative (µm)
7.0 - 11.3
Expand
Collapse
Coating type
ZA
Coating class
95
Standard
EN 10346
Closest in EN standard, informative 1)
ZA95
Coating mass per side, single spot test (g/m2)
—
Thickness per side informative (µm)
7.0 -
Expand
Collapse
Coating type
ZA
Coating class
130
Standard
EN 10346
Closest in EN standard, informative 1)
ZA130
Coating mass per side, single spot test (g/m2)
—
Thickness per side informative (µm)
10.0 -
Expand
Collapse
Coating type
EG
Coating class
12/12
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE25/25
Coating mass per side, single spot test (g/m2)
12 - 32
Thickness per side informative (µm)
1.7 - 4.5
Expand
Collapse
Coating type
EG
Coating class
18/18
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
18 - 38
Thickness per side informative (µm)
2.5 - 5.4
Expand
Collapse
Coating type
EG
Coating class
29/29
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE50/50
Coating mass per side, single spot test (g/m2)
29 - 49
Thickness per side informative (µm)
4.1 - 6.9
Expand
Collapse
Coating type
EG
Coating class
47/47
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE75/75
Coating mass per side, single spot test (g/m2)
47 - 61
Thickness per side informative (µm)
6.6 - 8.6
Expand
Collapse
Coating type
EG
Coating class
50/50
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
50 - 70
Thickness per side informative (µm)
7.0 - 9.9
Expand
Collapse
Coating type
EG
Coating class
53/53
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
53 - 73
Thickness per side informative (µm)
7.5 - 10.3
Expand
Collapse
Coating type
EG
Coating class
60/60
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
60 - 80
Thickness per side informative (µm)
8.5 - 11.3
Expand
Collapse
Coating type
EG
Coating class
65/65
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE100/100
Coating mass per side, single spot test (g/m2)
65 - 85
Thickness per side informative (µm)
9.2 - 12.0
Expand
Collapse
Coating type
EG
Coating class
70/70
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
70 - 90
Thickness per side informative (µm)
9.9 - 12.7
Expand
Collapse
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For GI and GA the closest informative value refers to EN 10346. For EG to EN 10152.
Surface Treatments
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI, GA, ZA): available as oiled and/or chemically passivated.
Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
Fabrication and Other Recommendations
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Docol® dual phase steel product offer
Docol® 500DP dual phase
Docol® 600DP dual phase
Docol® 800DP dual phase
Docol® 1000DP dual phase
Conteúdo relacionado
-
Estoque de amostras
Quer descobrir aplicações automotivas exclusivas, experimentar novos métodos de produção ou criar componentes mais leves e capazes de aumentar a eficiência do combustível, de resistir a colisões e com melhor sustentabilidade?
-
Dados de conformação para os aços AHSS Docol®