Docol® 500DP dual phaseMore about dual phase steel
Download data sheet
Download data sheet
Docol 500DP dual-phase steel possesses good formability and weldability and is suitable for car safety components such as reinforcements. This steel undergoes special heat treatment, producing mainly two phase structure. Ferrite that imparts unique forming properties represents one phase, and martensite that accounts for the strength represents the other phase. Bainite may be present as complementary phase.
Cold rolled / UC: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI, GA, ZA: thickness 0.70-3.00 mm, width up to 1520 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
||Yield strength Rp0.2
|Tensile strength Rm
|Min. inner bending radius for a 90° bend 2)|
|Docol CR290Y490T-DP||VDA 239-100||UC||L||290 - 380||490 - 600||24||0.19||0.15||30||0.0 x t|
|VDA 239-100||GI, GA*, ZA||L||290 - 380||490 - 600||24 1)||0.19||0.15||30||0.5 x t|
|Docol CR230Y500T-DL||SSAB||UC||T||230 - 300||500 - 600||24||—||—||—||0.0 x t|
|Docol CR290Y500T-DP||SSAB||UC||T||290 - 370||500 - 600||20||—||—||—||0.0 x t|
*Available upon request.
1) For GA coatings the minimum elongation value is reduced by 2 units.
2) In some cases tight bending radius may cause micro-cracking of the coating in the bend area. Where design permits, users are encouraged to employ larger radius. For GA coatings the minimum elongation value is reduced by 2 units.
|Docol CR290Y490T-DP||UC||0.10||0.50||1.00||0.025||0.010||From 0.015||0.10||—||—|
|GI, GA*, ZA||0.14||0.50||1.80||0.050||0.010||0.015 - 1.0||0.15||1.00||0.005|
|Docol CR230Y500T-DL||UC||0.08||0.40||1.80||0.025||0.010||From 0.015||0.10||—||—|
|Docol CR290Y500T-DP||UC||0.10||0.50||1.00||0.025||0.010||From 0.015||0.10||—||—|
Cold rolled (UC): Tolerances in accordance to EN 10131.
Hot-dip galvanized (GI, GA, ZA): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Galvannealed coating (GA) is a zinc-iron alloy coating having an iron content of approximately 10%. Galvannealed is produced by post-heat treatment in continuous hot-dip coating process. Galvannealed provides excellent resistance weldability and corrosion protection of painted products.
Galfan coating (ZA) is a zinc-aluminium alloy coating having the eutectic composition approximately of 95% Zn and 5% Al. Galfan is produced in continuous hot-dip coating process. Galfan has better anticorrosive and forming properties than conventional hot-dip zinc coating (GI).
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
|Coating type||Coating class||Standard||Closest in EN 10346, informative||Coating mass per side, single spot test (g/m2)||Thickness per side informative (µm)|
|GI||40/40||VDA 239-100||Z100||40 - 60||5.6 - 8.5|
|GI||50/50||VDA 239-100||—||50 - 70||7.0 - 9.9|
|GI||60/60||VDA 239-100||Z140||60 - 90||8.5 - 12.7|
|GI||70/70||VDA 239-100||—||70 - 100||9.9 - 14.1|
|GI||85/85||VDA 239-100||—||85 - 115||12.0 - 16.2|
|GI||115/115||VDA 239-100||Z275||115 - 155||16.2 - 21.8|
|GA||40/40||VDA 239-100||ZF100||40 - 60||5.6 - 8.5|
|GA||50/50||VDA 239-100||ZF120||50 - 80||7.0 - 11.3|
|ZA||95||EN 10346||ZA95||—||7.0 -|
|ZA||130||EN 10346||ZA130||—||10.0 -|
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings are available upon request.
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI, GA, ZA): available as oiled and/or chemically passivated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.