Docol® 1000CP complex phase
More about complex phase steelDownload data sheet
General Product Description
Docol® 1000CP is made for cold forming and allows for a tight bending radius on high-strength applications. These steels are characterized by both a high yield strength and an improved cleanliness, which allows for a tight radius.
Dimension Range
Cold rolled / UC, EG: thickness 0.50-2.10 mm, width up to 1527 mm.
Cold rolled / GI: thickness 0.95-2.00 mm, width up to 1250 mm.
Hot rolled / UC: thickness 2.50-4.50 mm, width up to 1510 mm.
Slit strip and cut to length sheets are available upon request.
Grade and coating specific restrictions on available dimensions may occur.
Mechanical Properties
Hide/Show specific columns Edit
Select columns to display
| Standard | Coating | Test direction |
Yield strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Elongation A80 (min %) |
Elongation A50 (min %) |
BH2 (min MPa) |
|
|---|---|---|---|---|---|---|---|---|
| Docol CR780Y980T CP | VDA 239-100 | UC, EG, GI | L | 780 - 950 | 980 - 1140 | 6 1) | — | 30 |
| Docol Roll 1000 | SSAB | UC, EG | T | 800 - 950 | 980 - 1140 | 6 | — | 30 |
| Docol Roll 1000HY | SSAB | UC, EG | T | 850 - | 1000 - 1200 | 5 | — | 30 |
| Docol HR720Y950T CP | SSAB | UC* | L | 720 - 900 | 950 - 1130 | — | 10 | 30 |
Compare parameters
Select one parameter to compare
Comparison
Docol CR780Y980T CP
Standard
VDA 239-100
Coating
UC, EG, GI
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
780 - 950
Tensile strength Rm
(MPa)
(MPa)
980 - 1140
Elongation A80
(min %)
(min %)
6 1)
Elongation A50
(min %)
(min %)
—
BH2
(min MPa)
(min MPa)
30
Expand
Collapse
Docol Roll 1000
Standard
SSAB
Coating
UC, EG
Test direction
T
Yield strength Rp0.2
(MPa)
(MPa)
800 - 950
Tensile strength Rm
(MPa)
(MPa)
980 - 1140
Elongation A80
(min %)
(min %)
6
Elongation A50
(min %)
(min %)
—
BH2
(min MPa)
(min MPa)
30
Expand
Collapse
Docol Roll 1000HY
Standard
SSAB
Coating
UC, EG
Test direction
T
Yield strength Rp0.2
(MPa)
(MPa)
850 -
Tensile strength Rm
(MPa)
(MPa)
1000 - 1200
Elongation A80
(min %)
(min %)
5
Elongation A50
(min %)
(min %)
—
BH2
(min MPa)
(min MPa)
30
Expand
Collapse
Docol HR720Y950T CP
Standard
SSAB
Coating
UC*
Test direction
L
Yield strength Rp0.2
(MPa)
(MPa)
720 - 900
Tensile strength Rm
(MPa)
(MPa)
950 - 1130
Elongation A80
(min %)
(min %)
—
Elongation A50
(min %)
(min %)
10
BH2
(min MPa)
(min MPa)
30
Expand
Collapse
*Available upon request.
The testing of mechanical properties of electrogalvanized products is conducted without coating.
1) Decreased minimum elongation values apply for product thickness t < 0.60 mm (minus 2 units).
Chemical Composition (ladle analysis)
Hide/Show specific columns Edit
Select columns to display
| Coating | C (max %) |
Si (max %) |
Mn (max %) |
P (max %) |
S (max %) |
Al (%) |
Nb+Ti (max %) |
Cr+Mo (max %) |
B (max %) |
Cu (max %) |
|
|---|---|---|---|---|---|---|---|---|---|---|---|
| Docol CR780Y980T CP | UC, EG, GI | 0.23 | 1.00 | 2.70 | 0.050 | 0.010 | 0.015 - 1.00 | 0.15 | 1.00 | 0.005 | 0.20 |
| Docol Roll 1000 | UC, EG | 0.16 | 0.40 | 1.80 | 0.020 | 0.010 | From 0.015 | 0.10 | — | — | — |
| Docol Roll 1000HY | UC, EG | 0.16 | 0.40 | 1.80 | 0.020 | 0.010 | From 0.015 | 0.10 | — | — | — |
| Docol HR720Y950T CP | UC* | 0.18 | 1.00 | 2.20 | 0.050 | 0.010 | 0.015 - 1.2 | 0.25 | 1.00 | 0.005 | 0.25 |
Compare parameters
Select one parameter to compare
Comparison
Docol CR780Y980T CP
Coating
UC, EG, GI
C
(max %)
(max %)
0.23
Si
(max %)
(max %)
1.00
Mn
(max %)
(max %)
2.70
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.00
Nb+Ti
(max %)
(max %)
0.15
Cr+Mo
(max %)
(max %)
1.00
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.20
Expand
Collapse
Docol Roll 1000
Coating
UC, EG
C
(max %)
(max %)
0.16
Si
(max %)
(max %)
0.40
Mn
(max %)
(max %)
1.80
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
From 0.015
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
—
B
(max %)
(max %)
—
Cu
(max %)
(max %)
—
Expand
Collapse
Docol Roll 1000HY
Coating
UC, EG
C
(max %)
(max %)
0.16
Si
(max %)
(max %)
0.40
Mn
(max %)
(max %)
1.80
P
(max %)
(max %)
0.020
S
(max %)
(max %)
0.010
Al
(%)
(%)
From 0.015
Nb+Ti
(max %)
(max %)
0.10
Cr+Mo
(max %)
(max %)
—
B
(max %)
(max %)
—
Cu
(max %)
(max %)
—
Expand
Collapse
Docol HR720Y950T CP
Coating
UC*
C
(max %)
(max %)
0.18
Si
(max %)
(max %)
1.00
Mn
(max %)
(max %)
2.20
P
(max %)
(max %)
0.050
S
(max %)
(max %)
0.010
Al
(%)
(%)
0.015 - 1.2
Nb+Ti
(max %)
(max %)
0.25
Cr+Mo
(max %)
(max %)
1.00
B
(max %)
(max %)
0.005
Cu
(max %)
(max %)
0.25
Expand
Collapse
* Available upon request.
Tolerances
Cold rolled (UC, EG): Tolerances in accordance to EN 10131.
Hot rolled (UC): Tolerances in accordance to EN 10051.
Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.
Customized dimensional and shape tolerances are available upon request.
Coatings
The metal coating options for Docol products include:
Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.
Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.
Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).
Hide/Show specific columns Edit
Select columns to display
| Coating type | Coating class | Standard | Closest in EN standard, informative 1) | Coating mass per side, single spot test (g/m2) | Thickness per side informative (µm) |
|---|---|---|---|---|---|
| GI | 40/40 | VDA 239-100 | Z100 | 40 - 60 | 5.6 - 8.5 |
| GI | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
| GI | 60/60 | VDA 239-100 | Z140 | 60 - 90 | 8.5 - 12.7 |
| GI | 70/70 | VDA 239-100 | — | 70 - 100 | 9.9 - 14.1 |
| GI | 85/85 | VDA 239-100 | — | 85 - 115 | 12.0 - 16.2 |
| GI | 115/115 | VDA 239-100 | Z275 | 115 - 155 | 16.2 - 21.8 |
| EG | 12/12 | VDA 239-100 | ZE25/25 | 12 - 32 | 1.7 - 4.5 |
| EG | 18/18 | VDA 239-100 | — | 18 - 38 | 2.5 - 5.4 |
| EG | 29/29 | VDA 239-100 | ZE50/50 | 29 - 49 | 4.1 - 6.9 |
| EG | 47/47 | VDA 239-100 | ZE75/75 | 47 - 61 | 6.6 - 8.6 |
| EG | 50/50 | VDA 239-100 | — | 50 - 70 | 7.0 - 9.9 |
| EG | 53/53 | VDA 239-100 | — | 53 - 73 | 7.5 - 10.3 |
| EG | 60/60 | VDA 239-100 | — | 60 - 80 | 8.5 - 11.3 |
| EG | 65/65 | VDA 239-100 | ZE100/100 | 65 - 85 | 9.2 - 12.0 |
| EG | 70/70 | VDA 239-100 | — | 70 - 90 | 9.9 - 12.7 |
Compare parameters
Select one parameter to compare
Comparison
Coating type
GI
Coating class
40/40
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z100
Coating mass per side, single spot test (g/m2)
40 - 60
Thickness per side informative (µm)
5.6 - 8.5
Expand
Collapse
Coating type
GI
Coating class
50/50
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
50 - 70
Thickness per side informative (µm)
7.0 - 9.9
Expand
Collapse
Coating type
GI
Coating class
60/60
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z140
Coating mass per side, single spot test (g/m2)
60 - 90
Thickness per side informative (µm)
8.5 - 12.7
Expand
Collapse
Coating type
GI
Coating class
70/70
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
70 - 100
Thickness per side informative (µm)
9.9 - 14.1
Expand
Collapse
Coating type
GI
Coating class
85/85
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
85 - 115
Thickness per side informative (µm)
12.0 - 16.2
Expand
Collapse
Coating type
GI
Coating class
115/115
Standard
VDA 239-100
Closest in EN standard, informative 1)
Z275
Coating mass per side, single spot test (g/m2)
115 - 155
Thickness per side informative (µm)
16.2 - 21.8
Expand
Collapse
Coating type
EG
Coating class
12/12
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE25/25
Coating mass per side, single spot test (g/m2)
12 - 32
Thickness per side informative (µm)
1.7 - 4.5
Expand
Collapse
Coating type
EG
Coating class
18/18
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
18 - 38
Thickness per side informative (µm)
2.5 - 5.4
Expand
Collapse
Coating type
EG
Coating class
29/29
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE50/50
Coating mass per side, single spot test (g/m2)
29 - 49
Thickness per side informative (µm)
4.1 - 6.9
Expand
Collapse
Coating type
EG
Coating class
47/47
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE75/75
Coating mass per side, single spot test (g/m2)
47 - 61
Thickness per side informative (µm)
6.6 - 8.6
Expand
Collapse
Coating type
EG
Coating class
50/50
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
50 - 70
Thickness per side informative (µm)
7.0 - 9.9
Expand
Collapse
Coating type
EG
Coating class
53/53
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
53 - 73
Thickness per side informative (µm)
7.5 - 10.3
Expand
Collapse
Coating type
EG
Coating class
60/60
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
60 - 80
Thickness per side informative (µm)
8.5 - 11.3
Expand
Collapse
Coating type
EG
Coating class
65/65
Standard
VDA 239-100
Closest in EN standard, informative 1)
ZE100/100
Coating mass per side, single spot test (g/m2)
65 - 85
Thickness per side informative (µm)
9.2 - 12.0
Expand
Collapse
Coating type
EG
Coating class
70/70
Standard
VDA 239-100
Closest in EN standard, informative 1)
—
Coating mass per side, single spot test (g/m2)
70 - 90
Thickness per side informative (µm)
9.9 - 12.7
Expand
Collapse
Docol metal coated products are available with surface quality for unexposed applications.
In addition to these coating masses, OEM specific coatings and single sided EG coatings are available upon request.
1) For GI and GA the closest informative value refers to EN 10346. For EG to EN 10152.
Surface treatments
Uncoated (UC): available as oiled.
Hot-dip galvanized (GI): available as oiled and/or chemically passivated.
Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.
All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr6+). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.
Fabrication and Other Recommendations
For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.
Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.
Docol® Complex Phase steel product offer
Docol® 600 CP complex phase
Docol® 800CP complex phase
Docol® 1000CP complex phase
Docol® 1200CP complex phase
Related content
-
AHSS trial material stock
Want to discover unique automotive applications for AHSS materials? Try new production methods? Or create lighter components that can improve fuel efficiency, crash-worthiness and sustainability?
-
Recommended AHSS steels for car applications
Docol® steel grades serve specific design purposes and are chosen by designers for a wide range of applications and used by OEMs and tier suppliers in millions of vehicles around the world.
-
Forming data for Docol® AHSS steels
Existing Docol® customers get 24/7 access to the forming data you need to help in your selection and simulation of automotive advanced high strength steels.